综述了国内外近期在亚稳态孔蚀行为的研究方法,亚稳态小孔形核、生长的统计规律,亚稳态蚀孔生长和再钝化过程的机制及控制因素,亚稳态蚀孔向稳定蚀孔转变的临界条件等方面的研究进展,并对进一步的研究作出了展望.
参考文献
[1] | Williams D E, Westcott C, Fleischmann M. J. Electrochem. Soc., 1985,132:1796 |
[2] | Williams D E, Westcott C, Fleischmann M. J. Electrochem. Soc., 1985,132:1804 |
[3] | Williams D E, Westcott C, Fleischmann M. J. Electroanal. chem., 1984,180:549 |
[4] | Frankel G S, Stockert L, Hunkeler F, Boehni H. Corrosion, 1987,48:428 |
[5] | Pistorius P C, Burstein G T. Phil. Trans. R. Soc. Lond. A, 1992,341:531 |
[6] | Pistorius P C, Burstein G T. Mater. Sci. Forum, 1992,111:429 |
[7] | Pistorius P C, Burstein G T. Corros. Sci., 1992,33:1885 |
[8] | Williams D E, Stewart J, Balkwill H. Corros. Sci., 1994,36:1213 |
[9] | 半田隆夫,宫田惠守,高泽寿佳.防食技术,1989,38:529 |
[10] | Stewart J, Williams D E. Corros. Sci., 1992,33:457 |
[11] | Laycock N J, Stewart J, Newman R C. Corros. Sci., 1997,39:1791 |
[12] | Bertocci U, Ye Y. J. Electrochem. Soc., 1984,131:1011 |
[13] | Bertocci U, Koike M, Leigh S, et al. J. Electrochem. Soc., 1986,133:1782 |
[14] | Bargeron C B, Givens R B. J. Electrochem. Soc., 1982,129:340 |
[15] | Uruchurtu J C, Dawson J L. Corrosion, 1987,43:19 |
[16] | Pistorius P C. Corrosion, 1997,53:273 |
[17] | Fukuda T, Mizuno T. Corros. Sci., 1996,38:1085 |
[18] | Hong T, Walter G W, Nagamo M. Corros. Sci., 1996,38:1525 |
[19] | Hong T, Nagamo M. Corros. Sci., 1997,39:285 |
[20] | Hong T, Nagamo M. Corros. Sci., 1997,39:961 |
[21] | Hong T, Nagamo M. Corros. Sci., 1997,39:1665 |
[22] | Schmuki P, Bohni H. J. Electrochem. Soc., 1992,139:1908 |
[23] | Shibata T, Takeyama T. Corrosion, 1977,33: 243 |
[24] | Gabrielli C, Huet P, Keddam M, Oltra R. Corrosion, 1990,46: 266 |
[25] | Gabrielli C, Huet P, Keddam M. Electrochemical and Optical Techniques for the Study and Monitoring of Metallic Corrosion, Ferreira M G S, Melendres C A(eds.), Kluwer Academic Publishers, 1991,135 |
[26] | Mola E E, Mellein B, Rodriguez E M, et al. J. Electrochem. Soc., 1990,137:1384 |
[27] | Burstein G T, Ilevbare G O. Corros. Sci., 1996,38: 2257 |
[28] | Shibata T. Corrosion, 1996,52: 813 |
[29] | Pistorius P C, Burstein G T. Corros. Sci., 1994,36:525 |
[30] | Burstein G T, Pistorius P C. Corrosion, 1995,51:380 |
[31] | Bohni H, Suter T, Schreyer A. Electrochemica Acta, 1995,40:31 |
[32] | 坂入正敏,西方笃,水流彻.防食技术,1991,40:183 |
[33] | Burstein G T, Pistorius P C, Mattin S P. Corros. Sci., 1993,35:57 |
[34] | 左禹.中国腐蚀与防护学报,1995,15:28 |
[35] | Zuo Y, Fu S. Corros. Sci., 1997,39:465 |
[36] | Zuo Y, Fu S. Corrosion, 1998,54:313 |
[37] | Holliger R, Bohni H. Computor Aided Acquisition and Analysis of Corrosion Data, Kendig M W, Bertocci U, Strutt J E(eds.), The Electrochemical Soc., Pennington, N.J., 1985,3:200 |
[38] | 水流彻,坂入正敏,防食技术,1990,39:355 |
[39] | Zuo Y, Du H, Xiong J, et al. Proc. The Fourth International Joint Symposium of CNU and BUCT, May 11, 1998, Taejon, 87 |
[40] | Pride S T, Scully J R, Hudson J L. J. Electrochem. Soc., 1994,141:3028 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%