7xxx系列Al合金应力腐蚀开裂的研究

刘继华 ^1, , 李荻 ^2, , 郭宝兰 ^3,

1.北京航空航天大学材料科学与工程系

2.北京航空航天大学材料科学与工程系

3.北京航空航天大学材料科学与工程系

基金项目: 国家重点基础研究发展计划(973计划)(G1999064909-3)

关键词：高强Al合金 , 应力腐蚀开裂 , 综述

INVESTIGATION OF STRESS CORROSION CRACKING OF 7XXX SERIES ALUMINUM ALLOYS

综述了7xxx系列Al合金的应力腐蚀开裂机理和影响应力腐蚀开裂行为的因素，讨论了应力腐蚀开裂过程的微观结构变化及其与应力腐蚀开裂敏感性的关系.在不降低合金力学性能的前提下，提高耐应力腐蚀开裂性将使该系合金有广泛的应用前景.

参考文献

[1]	Li Xiaomei, Starink M J. Mater. Sci. Forum, 2000, 331-337:1071
[2]	Liu John, Michael Kulak. Mater. Sci. Forum, 2000, 331-337:127
[3]	Fleck P, Calleros D, Madsen M, et al. Mater. Sci. Forum,2000, 331-337:649
[4]	Asaro R J, Tiller W A. Metall. Trans., 1972, 3:1789
[5]	Galvele J R.Corros. Sci., 1987,27:1
[6]	Sieradzki K, Friedersdorf F J.Corros. Sci., 1994,36:669
[7]	Holl H A. Corrosion, 1967, 23:173
[8]	DeArdo Jr A J, Townsend R D. Metall. Trans., 1970,1:2573
[9]	Landkof M, Gal- Or L. Corrosion, 1980,36:241
[10]	Gest R J, Troiano A R. Corrosion, 1974, 30:274
[11]	Speidel M O. Metall. Trans. A, 1975, 6:631
[12]	Pathania R S, Tromans D. Metall. Trans. A, 1981,12: 607
[13]	Scamans G M, Alani R, Swarm P R. Corros. Sci., 1976,16:443
[14]	Albrecht J, Thompson A W, Bernstein I M. Metall. Trans. A,1979, 10:1759
[15]	Albrecht J, Bemstein I M, Thompson A W. Metall. Trans. A,1982,13:811
[16]	Hardwick D A, Thompson A W, Bemstein I M. Metall.Trans. A, 1983,14:2517
[17]	Hardwick D A, Thompson A W, Bernstein I M. Corros. Sci.,1988, 28:1127
[18]	Scamans G M.Metall. Trans. A, 1980,11: 846
[19]	Najjar D, Magnin T, Warner T J. Mater. Sci. Eng. A, 1997,238: 293
[20]	Scully J R, Young Jr G A, Smith S W. Mater. Sci. Forum,2000, 331-337:1583
[21]	Zuhair M Gasem, Richard P Gangloff. Mater. Sci. Forum,2000, 331-337:1479
[22]	Wei R P, Pao P S, Hart R G, et al. Metall. Trsns. A, 1980,11:151
[23]	Stanzl S E, Mayer H R, Tschegg E K. Mater. Sci. Eng. A,1991,147:45
[24]	Lee Seong-Min, Pyun Su-I1, Chun Young-Gab. Metall.Trans. A, 1991,22:2407
[25]	Gong Bo, Lai Zuhan. Proc. of ICAA Ⅱ, Beijing, 1990. 657
[26]	Sedriks A J, Green J A S, Novak D L. Corrosion, 1971,27:198
[27]	H F de Jong. Corrosion, 1978, 34: 32
[28]	Tsai W-T, Duh J-B, Yeh J-J, et al. Corrosion, 1990,46:444
[29]	Sarkar B, Marek M, Starke E A. Metall. Trans. A, 1981,12:1939
[30]	Braun R. Corroaion, 1997, 53:467
[31]	Narasimha Rao B V. Metall. Trans. A, 1981,12:1356
[32]	Doig P, Flewitt P E J, Edington J W. Corrosion, 1977, 33:217
[33]	Tseng Mei-kuang, Liu Jun, Jin Zhen-hong. Proc. of ICAA Ⅱ, Bejing, 1990. 662
[34]	Wang Laishen. Proc. of ICAA II, Beijing, 1990. 687
[35]	Cina B. US Patent 3856584,1974
[36]	Park J K, Ardell A J. Metall. Trans. A, 1984,15:1531
[37]	Rajan K, Wallace W, Beddoes J C.J. Mater. Sci., 1982, 17:2817
[38]	Papazian J M. Mater. Sci. Eng., 1986, 79:97
[39]	Kanno M, Araki I, Cui Q. Mater. Sci. Technol., 1994, 10:599
[40]	Rajan K, Wallace W, Beddoes J C.J. Mater. Sci., 1982, 17:2817
[41]	Talianker M, Cina B.Metall. Trans. A, 1989,20:2087
[42]	Gong Bo, Lai Zuhan. Proc. of ICAA Ⅱ, Beijing, 1990. 657
[43]	Lin Zhaoqi, Jiang Wenhui, Yang Shenkun, et al. Proc. of ⅠCAA Ⅱ, Beijing, 1990. 480
[44]	Wert J A, Paton N E, Hamilton C H, et al. Metall. Trans. A,1981,12:1267
[45]	Tsai T C, Chuang T H. Mater. Sci. Eng. A, 1997, 225:135
[46]	Christodoulou L, Flowet H M. Acta Metall., 1980, 28:481
[47]	Yoder G R, Pao P S, Bayles R A. Scr. Metall. Mater., 1990,24:2285
[48]	Pao P S, Gill S J, Bayles R A. Scr. Metall. Mater., 1991, 25:2085
[49]	Femminella O P, Starink M J, Gunn S R, et al. Mater. Sci. Forum, 2000, 331-337:1255
[50]	Senatorova O G, Uksusnikov A N, Legoshina S F, et al.Mater. Sci. Forum, 2000, 331-337:1249
[51]	Milman Yu. V, Lotsko D V, Sirko O I. Mater. Sci. Forum,2000, 331-337:1107
[52]	Riddle Yancy W, Sanders Jr T H, Mater. Sci. Forum, 2000,331-337:799
[53]	Adler P N, Deisai R. Metall. Trans. A, 1977,8:1185

上一张下一张

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
刘继华李荻郭宝兰
在百度学术搜索
刘继华李荻郭宝兰
在万方数据库搜索
刘继华李荻郭宝兰
在CNKI搜索
刘继华李荻郭宝兰

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%