球磨80～200 h的Ni-Ag合金粉末经热压烧结后获得了晶粒尺寸小于50 nm的Ni-50Ag纳米晶块体材料,经热处理后其晶粒长大约至100 nm.在600℃的高温氧化时,合金呈现出不同的氧化膜结构及氧化增重速率.MA 80h Ni-50Ag和MA 200h Ni-50Ag合金在600℃空气氧化时均未形成选择性的外氧化膜,而形成了非平衡态复杂内氧化结构.热处理前,合金的氧化行为受晶粒尺寸以及合金内部缺陷,内应力等诸多因素的影响,导致MA80 h和200 h合金不同时间合金氧化速率常数相差较大.而经热处理后,主要是晶粒尺寸影响合金的氧化行为.
参考文献
| [1] | Massalski T B, Okamoto H, Subramanian P R et al. Eds. Binary Alloy Phase Diagrams, 2nd ed. ASM International, Materials Park, OH, 1990.64 |
| [2] | Hadjipanayis G C, Siegel R W. Nanophase materials, synthesis,properties, applications, Kluwer Academic Publishers, London,1994 |
| [3] | Zhao Z L, Zhao Y, Niu Y et al. J. all. Comp. 2000, 307: 254 |
| [4] | Kofstad F. High Temperature Corrosion, Elsevier Applied Science, London, 1988 |
| [5] | Z Liu, W Gao K L Dahm, F Wang. Acta Materialia, 1999, 46:1691 |
| [6] | G Chen, H Lou. Scripta Mater. 1999: 41,883 |
| [7] | A Atkinson. Prv. Modern Phys. 1985: 57,437 |
| [8] | E W Hart. Acta Met. 1957: 5,597 |
| [9] | Zhao Z, Wang C, Zhao Y et al. Proceeding of 2000 Powder Metallurgy of world congress, Tokyo, 1749 |
| [10] | F Wang. Oxid. Met. 1997:47,247 |
| [11] | Guruswamy S, Park S M, Hirth J P et al. Oxid Met, 1986,26:77 |
| [12] | Z L Zhao, Y Niu, F Gesmundo et al. Oxid. Met, 2000, 54 (5/6):557 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%