应用电化学交流阻抗技术(EIS)研究了AISI304不锈钢在3.5%NaCl溶液中的电化学行为及表面涂敷有机硅涂料后的电化学行为.结果表明,AISI304不锈钢在在开路电位下的交流阻抗表现为单容抗弧,在浸泡初期,随着时间的延长,耐蚀性提高,当浸泡120 d后,耐蚀性明显下降.不锈钢表面涂敷一层有机硅涂料后,EIS发生了较大变化,浸泡初期为单容抗弧,阻抗值明显增大,浸泡1天后表现为双容抗孤,而不锈钢裸样的始终表现为单容抗弧.
参考文献
| [1] | 杨武,顾濬祥,黎樵燊,等.金属的局部腐蚀[M].北京:化学工业出版社,1995.18. |
| [2] | 周宁琳.有机硅聚合物导论[M].北京:科技出版社,2000.137. |
| [3] | 张鉴清.富锌涂层的电化学阻抗谱特性[J].中国腐蚀与防护学报,1996,16(3):175. |
| [4] | Titz J, Wagner G H. Characterization of organic coatings on metal substrates by electrochemical impedance spectroscopy[ J ].Corrosion, 1990, 46(3) :221. |
| [5] | Mansfeld F, Kending M. Determination of the long term corrosion behavior of coated steel with A. C. impedance measurements[ J ]. Corros. Sci., 1983, 23(2) :317. |
| [6] | Yin K M, Wah Z. Electrochemical impedance study of the degradation of orgainc - coated copper[ J ]. Surface and coatings technology, 1998,106:167. |
| [7] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,1985.228. |
| [8] | Walter G W. A revew of impedance plot methods used for corrosion performance analysis of painted metals[J]. Corros. Sci.,1986, 26(9) :681. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%