用真空电弧熔炼制备了β(Nb-35Ti-6A1)和β+δ(Nb-30Ti-15A1、Nb-15Ti-11Al)Nb台金,研究了3种Nb合金1000℃静止空气中的连续氧化行为,采用金相显微镜、XRD和SEM分析了氧化膜的结构和组成.研究表明,由Nb2O5,金红石TiO2和-A12O3组成的混合氧化膜具有一定的保护作用,3种Nb-Ti-Al合金氧化动力学曲线均遵循抛物线规律;Nb-35Ti-6Al中的富Ti偏析区发生内氧化,而Nb-30Ti-15Al和Nb-15Ti-11Al中δ相的存在有利于降低氧在基体中的溶解和扩散,使β+δ两相合金的氧化性能优于β单相合金.
参考文献
| [1] | A Dollar, S Dymek. Microstructure and high temperature mechanical properities of mechanically alloyed Nb3Al-based eterials[J]. Intermetallics, 2003, (11): 341. |
| [2] | Yonosuke Murayama, Shuji Hanada. High temperature strength, fracture toughness and oxidation resistance of Nb-SiAl-Ti multiphase alloys[J]. Sci Tech of Adv Mater, 2002(3):145. |
| [3] | V K Sikka, E ALoria. Characteristics of a multicomponent NbTi-Al alloy via industrial-scale practice[J]. Mater Sci Eng,1997, A239/240: 745. |
| [4] | P R Subramanian, M G Mendiratta, D M Dimiduk, et al. Advanced intermetallic alloys-beyond gamma titanium aluminides [J]. Mater Sci Eng, 1997, A239/240:1. |
| [5] | T Tabaru, S Hanada. High temperature strength of Nb3Albased alloys[J]. Intermetallics, 1998, (6) :735. |
| [6] | R Gnanamoorthy, S Hanada. Microstructure and strength of binary and tantalum alloyed two-phase Nbss/Nb3Al base alloys [J]. Mater Sci Eng, 1996, A207:129. |
| [7] | Keith J Leonard, Joseph C Mishurda, Vijay K Vasudevan.Phase equilibria at 1100℃ in the Nb-Ti-Al system[J]. Intermetallics, 2000, 8 (9 - 11 ): 1257. |
| [8] | Dah-Liang Guan, Charlie R. Brooks, et al. Microstrcture and mechanical properties of as-cast and aged Nb-15at% Al-10at%Ti, - 25at % Ti and-40at % Ti alloys [J]. Intermetallics, 2002,(10) :441. |
| [9] | 徐祖耀.块状相变[J].热处理,2003,18(3):1. |
| [10] | 蓝兰.铌[M].北京:中国工业出版社,1964.152. |
| [11] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001.79. |
| [12] | 李铁藩.金属高温氧化和热腐蚀[M].北京:化学工业出版社,2003.139. |
| [13] | G H Meier, FS Pttit. The oxidation behavior o intermetallic compounds[J]. Mater Sci Eng, 1992, A153: 548. |
| [14] | 赵群,于永泗.铌基合金的抗高温氧化性研究[J].材料导报,2003,(2):29. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%