用丝束电极测量和缝隙腐蚀试验等方法研究X70钢和16 Mn钢在3种介质中点蚀和缝隙腐蚀方面的异同行为,发现在同样腐蚀环境下X70钢表面电位极差大于16 Mn钢,结合形貌观察可以肯定X70钢具有较强点蚀倾向.2种管道钢在较弱腐蚀溶液中缝隙腐蚀不明显,以平均腐蚀为主;在较强腐蚀溶液中,缝隙腐蚀和平均腐蚀同时发生.从缝隙腐蚀失重数据看,X70钢缝隙腐蚀平均失重稍大于16 Mn钢,但试验尚不能肯定两者在最大缝隙深度方面是否存在差异.
参考文献
| [1] | 杨锐鹏,翁永在.X70和16Mn钢土壤腐蚀行为比较:I电位和平均腐蚀速度[J].腐蚀科学与防护技术,2005,17(3):14. |
| [2] | ASTM Standard G61 -86, Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements for Localized Corrosion Susceptibility of Iron -, Nickel -, Cobalt -Based Alloys, Annual Book of ASTM Standard, 03.02, Philadelphia, PA, ASTM, 1997. |
| [3] | F Wenger, S Cheriet, and B Talhi, Electrochemical impedance of pits-influence of the pit morphology [J], Corrosion Science,1997, 39:1239. |
| [4] | R A Cottis, H A Al- Mazeedi and S. Turgoose, Measures for the identifical of localized corrosion from electrochemical noise measurements[J], Corrosion/2002, Paper No. 02329. |
| [5] | 张华民,邱于兵.用丝束电极研究对硝基苯甲酸钠引起的局部腐蚀[J]化学,1996,13(2):165. |
| [6] | 翁永基,赵海燕,用丝束电极(WBE)评价不锈钢在NaCI溶液中点蚀敏感性[J],中国腐蚀与防护学报,2003,23(6):165. |
| [7] | 曹楚南,腐蚀试验数据的统计分析[M],北京:化学工业出版社,1988.37 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%