通过电化学渗氢技术研究了施加不同阴极电位条件下含不同H2S浓度的3.5%NaCl溶液中X70管线钢的氢渗透行为.结果表明,稳态渗氢电流P∞随H2S浓度的增大而逐渐增大,但一定时间内,渗透过试样的氢原子摩尔数并不随之单调增加;氢原子的渗透受到阴极电位的控制,阴极电位越负,渗氢电流越大;在一定电位范围内,稳态渗氢电流P∞和一定时间内渗透过试样的氢原子摩尔数N与阴极电位呈线性关系.扩散系数与试验条件无关.
参考文献
[1] | Margot-Marette H, Bardou G, Charbonnier J C. The application of the slow strain rate test method for the development of linepipe steels resistant to sulphide stress cracking [ J ]. Corros Sci, 1987, 27:1009. |
[2] | Erlings J G, de groot H W, Nauta J. The effect of slow plastic and elastic straining on sulphide stress cracking and hydrogen embrittlement of 3.5% Ni steel and API 5L X60 pipeline steel[J]. Corros Sci, 1987, 27:1153. |
[3] | GB17378.4 - 1998. 海洋监测规范第4部分:海水分析[S]. |
[4] | Devnathan M A V, Stachurski Z. A technique for the evaluation of hydrogen embrittlement characteristics of electroplating baths[J]. J Electrochem Soc, 1963,110(8) :886. |
[5] | Yanliang Huang, Akira Nakajima, Atsushi Nishikata et al. Effect of mechanical deformation on permeation of hydrogen in iron[J]. ISIJ international, 2003, 43: 548. |
[6] | Berkowitz B J, Horowitz H H. The role of H2S in the corrosion and hydrogen embrittlement of steel [ J ]. J. Electrochem Soc,1982, 129: 468. |
[7] | Bockris J OM, McBreen J, Nanis L. The hydrogen evolution kinetics and hydrogen entry into α-iron[J]. J. Electrochem Soc,1965,112:1025. |
[8] | William H. Thomason. Quantitative measurement of hydrogen charging rates into steel surfaces exposed to seawater under varying cathodic protection levels[ J ]. MP, 1988, 27: 63. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%