用AFGROW软件计算了2024-T3铝合金的不同腐蚀损伤程度下的疲劳寿命,与实验数据比较吻合.建立了对腐蚀损伤和疲劳寿命分类的概率神经网络模型,输出结果表明:铝合金的失效模式:点蚀-晶间腐蚀-剥蚀,决定了腐蚀损伤和疲劳寿命的分布类型;对铝合金的腐蚀损伤和疲劳寿命,应用3种或2种分布类型,而非单一分布来表征其分布规律.
参考文献
| [1] | J J Medved,M Breton,P E Irving.Corrosion pit size distributions and fatigue lives - a study of the EIFS technique for fatigue design in the presence of corrosion [J].J fatigue,2004 (26) :71. |
| [2] | 谢伟杰,李荻,胡艳玲,等.LY12CZ和7075T7351铝合金在EXCO溶液中腐蚀动力学的统计规律[J].航空学报,1999,20(1):34. |
| [3] | 胡艳玲,李荻,郭宝兰.LY12CZ铝合金型材的腐蚀动力学统计规律研究及日历寿命预测方法探讨[J].航空学报,2000,21(Sup.):S53. |
| [4] | 任和,冯元生,王琛.运七机翼腐蚀失效模型及其可靠性分析[J].腐蚀科学与防护技术,1998,10(4):212. |
| [5] | Osama M Alyousif.Corrosion and corrosion fatigue of aluminum alloys[D].Lehigh University,April 2002.70. |
| [6] | 陈跃良,吕国志,段成美.服役条件下飞机结构腐蚀损伤概率模型研究[J].航空学报,2002,23:249. |
| [7] | R M Pidaparti,S Jayanti,C A Sowers.Classification,Distribu tion,and Fatigue Life of Pitting Corrosion for Aircraft Materials [J] .Journal of Aircraft,2002,39(3) :486. |
| [8] | Demuth H,Beale M.Neural Network Toolbox:For use with MATLAB,User's Guide[M].Mathworks Inc.1998.621. |
| [9] | Dolley EJ,Lee B,Wei RP.The effect of pitting corrosion on fatigue life [J].Fatigue Fract Eng Mater Struct,2000,23:555. |
| [10] | James A.Harter.Afgrow User Guide and Technical Manual[M].Wright Patterson AFB,2004.9. |
| [11] | Dale Cope.Corrosion Damage Assessment Framework [R].F9603 - 97 - C - 0349,Boeing ISDS Post - Production.1997.3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%