选择航空工业广泛使用的铝、铝合金及其涂层的试样,利用自行研制的Kelvin探头大气腐蚀测定仪、扫描电镜等设备,研究了纯铝试样随温、湿度变化,其表面电位的变化规律,测定了铝合金及涂层试样大气曝晒试验和周浸试验前后的表面电位、形貌,对铝、铝合金以及涂层的腐蚀规律进行了初步的探讨.结果表明,纯铝试样表面无可见液膜时,腐蚀电位随相对湿度增加逐渐下降;表面有可见液膜时,随着液层蒸发逐渐减薄,电位逐渐正移.铝合金裸材在北京大气环境下电位变化较小,且各个位置的电位基本相同.带涂层的试样优先在缺陷处发生腐蚀,并不断向周围扩展,涂层的剥离面积不断增大.涂层的铝合金,划痕处在腐蚀发生的初期腐蚀电位向负方向变化很快,但是随着时间的延长,腐蚀电位变化的速率减慢,并有向正方向移动的趋势.
参考文献
| [1] | M Stratmann.The investigation of the corrosion properties of metals,covered with absorbed eletrolyte-a new experimental technique[J].Corro.Sci.,1987,27:869. |
| [2] | M Stratmann,H Streckel.Monitoring of blistering of organic coatings by a contact-free measurement[J].Werkstoffe Und Korrosion,1992,43:316. |
| [3] | Shelgon Yee,R A Oriani,M Strantmann.Application of a Kelvin microprobe to the corrosion of metals in humid atmospheres[J].J.Electrochem.Soc.,1991,138(1):55. |
| [4] | A P Nazarov,D Thierry.Studies in theelectrical double layer at metal/polymer interfaces by scanning capacitive probe[J].Protection of Metals,2003,39:55. |
| [5] | M Doherty,J M Sykes.Micro-cells beneath organic lacquers:a study using scanning Kelvin probe and scanning acoustic microscopy[J].Corros.Sci.,2004,46:1265. |
| [6] | 孙志华,刘明辉,李家柱,等.大气腐蚀电化学测定研究[J].航空材料学报,2000,20(3):120. |
| [7] | 孙志华,李家柱,刘明辉,等.Kelvin探头振动电容法技术在大气腐蚀中的应用[J].腐蚀科学与防护技术,2001,13(增刊)(11):451. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%