根据不锈钢钝化膜的生长过程和钼酸盐的电化学反应机理,调制了相应的交变电场,并获得钼酸盐修饰的不锈钢钝化膜;用XPS和电化学测试研究了钝化膜的组成和性能.结果表明:调制相应的交变电场可以获得所需的组成结构和性能的产物;膜层具有理想的组成结构和性能,其耐蚀性得到提高.
参考文献
| [1] | W Yang,R C Ni,H Z Hua,et al.The behavior of chromium and molybdenum in the propagation process of localized corrosion of steel[J].Corrosion Science,1984,24 (8):934. |
| [2] | C R Clayton,Y C Lu.A bipolar model of the passivity of stainless steel-Ⅱ the mechanism of MoO42-formation and incorporation[J].Corrosion Science,1989,29(7):881. |
| [3] | J Jefferies,B Budcher.A new look at molybdate[J].Materials Performace,1992,31(5):50. |
| [4] | M S Vukasovich.Applications for the Versatile Molybdate Inhibition[J].Materials Performance,1990,29(5):48. |
| [5] | G L Song,C N Cao.Effect of AC-modulated passivation and post treatment on composition and stability of passive films[J].Corrosion,1993,49(4):271. |
| [6] | 方景礼,刘琴,韩克平,等.不锈钢上紫红色钼酸盐转化膜的研究[J].应用化学,1995,12(3):1. |
| [7] | T E Evans,A C Hart,H James,et al.A new process for coloring stainless steel[J].Trans.IMF,1972,50:77. |
| [8] | M A Stranick.The corrosion inhibition of metals by molybdate (Part Ⅰ,Mild steel)[J].Corrosion,1984,40(6):296. |
| [9] | 宋光铃,曹楚南,林海潮.不锈钢钝化-过钝化区电极过程的交流阻抗分析[J].中国腐蚀与防护学报,1993,13:1. |
| [10] | W C Moshier,G D Davis.Interaction of molybdate anions with the passive film on aluminum[J].Corrosion,1990,46 (1):43. |
| [11] | A R Brooks,C R Clayton,K Doss,Y C Lu.On the role of Cr in the passivity of stainless steel[J].J.Electrochem.Soc.,133(12):2459. |
| [12] | Zhang Junxi,Chen Jian,Qiao Yinan,et al.The growth mechanism of the colored passive film form on 304 stainless steel in sulferic solution without Cr6+ ion by using A.V[J].Passivation,Trans.IMF,1999,77:106. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%