综述了在有阴极保护的条件时剥离涂层下缝隙内电位电流的分布和化学环境的变化、阴极保护防止缝隙腐蚀的机理、微生物腐蚀的机理以及前人提出的关于剥离涂层下微生物腐蚀与阴极保护相互作用的规律,并展望了对于解决剥离涂层下微生物腐蚀难题需进一步的实验研究.
参考文献
| [1] | 夏双辉,戚明友,李建秀,等.微生物腐蚀机理及对埋地管道腐蚀防护的影响[J].全面腐蚀控制.2005,19(3):27. |
| [2] | 李正奉,毛旭辉,甘复兴,等.阴极保护下缝隙内的电流分布[J].中国腐蚀与防护学报,2000,20(6):338. |
| [3] | Chin DT,Sabde GM.Current distribution and electrochemical environment in a cathodically protced crevice[J].Corrosion,1999,55(3):229. |
| [4] | 李正奉,毛旭辉,甘复兴,等.阴极保护下缝隙内的电位分布[J].中国腐蚀与防护学报,2000,20(3):129. |
| [5] | Zhengfeng Li,Fuxing Gan,Xuhui Mao.A study on cathodic protection against crevice corrosion in dilute solutions[J].Corrosion Science,2002,44(4):689. |
| [6] | Thomas R Jack,Martyn J Wilmott.External corrosion of line pipe-A summary of research activities performed since 1983[J].Corrosion,1995,51 (5):354. |
| [7] | Jack T R.Sampling and Analytical Methods for Corrosion Products[M].Alberta:NACE Calgary section workshop on pipeline integrity.1993. |
| [8] | 廖强强.微生物腐蚀机制及检测方法[J].华东电力,2003,31(9):40. |
| [9] | 魏宝明主编.金属腐蚀理论及应用[M].北京:化学工业出版社,1984.172. |
| [10] | 刘靖,侯宝利,郑家燊,等.硫酸盐还原菌腐蚀研究进展[M].材料保护2001,34(8):8. |
| [11] | M D Orton.The effectiveness of cathodic protection under unbonded coatings on pipelines[J].Materials Performance,1985,24(6):17. |
| [12] | J McCoy.Cathodic protection on the dampier to perth pipelineaustralia[J].Materials Performance,1989,28 (2):16. |
| [13] | A C Toncre.On achieving polarization beneath unbonded pipe coating[J].Materials Performance,1984,23 (8):22. |
| [14] | J J Perdomo,I Song.Chemical and electrochemical conditions on steel under disbanded coatings:the effect of previously corrode surfaces and wet and dry cycles[J].Corrosion Science,2001,43(3):515. |
| [15] | M H Peterson,T J Lennox.A study of cathodic polarization and pH changes in metal crevices[J].Corrosion,1973,29 (10):406. |
| [16] | F Gan,Z W Sun.Cathodic protection to mitigate external corrosion[J].Corrosion,1994,50(10):804. |
| [17] | K M Fink,J H Payer,R F Savinell.Mitigation of corrosion by modification of the environment beneath disbonded coatings on pipelines,Corrosion/93,Houston:NACE1993.paper no.578. |
| [18] | R R Fessler,A J Markworthy,R N Parkins.Cathodic protection levels under disbonded coatings[J].Corrosion,1983,39(1):20. |
| [19] | B W Cherry,A N Gould.Pitting corrosion of nominally protected Land-Based pipelines[J].Materials performance,1990,29(8):22. |
| [20] | J J Perdomo,I Song.Chemical and electrochemical conditions on steel under disbanded coatings:the effect of applied potential,solution resistivity,crevice thickness,and holiday size[J].Corrosion Science,2000,42 (8):1389. |
| [21] | J Pikas.Case histories of external microbiologically influenced corrosion underneath disbanded coatings[J].Corrosion,1996.354. |
| [22] | Li S,Kim Y.Microbiologicallly influenced corrosion of carbon steel exposed to anaerobic soil[J].Corrosion,2001,57 (9):815 |
| [23] | C DuaneTracy.Disbonded coatings influence CP,pipeline risk assessment,[J] Pipeline & gas industry,1997,80 (2):27 |
| [24] | Kajiyama F,Okamura K.Evaluating cathodic protection reliability on steel in microbiologically active soils[J].Corrosion,1999,55 (1):74. |
| [25] | Grobe S,Prinz W,Schoneich HG,Wingender J.Influence of sulfate-reducing bacteria on cathodic protection[J].Werkstoffe und corrosion-materials and corrosion,1996,47(8):413. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%