通过模拟某气田CO2/H2S共存腐蚀介质环境,对比研究了SM80SS油管钢在加与未加缓蚀剂时的腐蚀特征.结果表明,在未加自制缓蚀剂TG500的腐蚀溶液中,SM80SS油管钢的腐蚀速率随H2S分压的升高而缓慢增加;当溶液中加入TG500(浓度200 mg/L)后,SM80SS钢的腐蚀速率显著降低、且随着H2S分压的增加明显下降,而缓蚀效率却呈上升趋势,均达90%以上.
参考文献
| [1] | Lyer R N,Takeuchi I.Hydrogen sulfide effect on hydrogen entry into iron[J].Corrosion,1990,46 (7):415. |
| [2] | Nesic S,Lunde L.Carbon dioxide corrosion of carbon steel in two -phase flow[J].Corrosion,1994,50(9):717. |
| [3] | Fred F,Lyle Jr.CO2/H2S Corrosion under Wet gas Pipeline Conditions in The Presence of Bicarbonate,Chloride,and Oxygen[C].Corrosion/1998,USA San Diego:NACE,1998.011. |
| [4] | Raymond B,Goodfellow.A Case Study of The Design and Operation of High CO2 Production With H2S[C].Corrosion/2001,USA Houston:NACE,2001,paper No.047. |
| [5] | Kvarekval J,Nyborg R and Seiersten M.Corrosion Product Films on Carbon Steel in SEMI -Sour CO2/H2S Environments[C].Corrosion/2002,USA DenVer:NACE,2002.296. |
| [6] | 张玉芳.用于含CO2/H2S环境的缓蚀剂研制[J].石油与天然气化工,2005,34(5):407. |
| [7] | 杨怀玉,陈家坚,曹楚南,等.酸性H2S溶液中碳钢的腐蚀行为及硫化物膜的生长[J].中国腐蚀与防护学报,2000,20(1):1. |
| [8] | 郑家燊,吕战鹏.二氧化碳腐蚀机理及影响因素[J].石油学报,1995,16(3):134. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%