采用俄SE-5.01振动式电火花表面强化机,以金属Cr作为强化电极材料,以炮钢PCrNi3MoVA作为基体材料,研究了强化层的特征、硬度、回火硬度、耐磨性以及900℃的高温氧化行为.结果表明,强化层是冶金结合的梯度涂层,强化层硬度和耐磨性较基体有很大的提高,回火析出的硬质相使其具有很好的热硬性,900℃连续氧化100 h后,强化层表面只有局部存在Cr2O3保护膜.
参考文献
| [1] | 路德维希·施蒂费尔编,杨葆新,袁亚雄,等译.火炮发射技术[M].北京:机械工业出版社,1998.280. |
| [2] | Johnson R N,Sheldon G L.Advances in the electrespark deposi-tion coating process[J].Journal of Vacuum Science & Technolo-GY A:Vacuum,Surfaces,and Films.1986(1):19. |
| [3] | WANG Rui-jun,QIAN Yi-yu,LIU Jun.Interface behavior study of WC92-Co8 eoating produced by electrespark deposition[J].China Welding,2004,13(1):61. |
| [4] | 张健,郭策安.CrNi3MoVA钢表面电火花沉积Cr的试验研究[J].沈阳理工大学学报,2006,(3):22. |
| [5] | 潘国顺,曲敬信,邵菏生.脉冲放电电火花熔涂W、Cr工艺及强化层性能研究[J].铸造.2000,49(1):655. |
| [6] | 夏卿坤,刘白,胡冠昱.三种纯金属电极脉冲电火花放电熔涂强化试验[J].新技术新工艺,2004(8):27. |
| [7] | Habig,K H 著,严立译.材料的磨损与硬度[M].北京:机械工业出版社,1990.54. |
| [8] | Teptenko M A,Lavrenko V A,Podehemyacva I A,et al.Inereas-ing the corrosion and wear resistance of chromium steel by dee-trospark alloying with an Ain-ZrB2-ZrSi2 electrode[J].Power Metallurgy and Ceramics,2003,42:129. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%