采用载波处理方法,用0.25 mol/L Na2SO4+0.1 mol/L NaOH作为载波处理溶液,对纯镁试样进行载波处理,通过正交试验确定载波处理的最佳工艺参数;用扫描电子显微镜(SEM)观察载波处理后试样的表面形貌;用FirstTen Angstroms(FTA)仪器测量蒸馏水纯镁的接触角并计算出表面能;用电化学方法研究了在0.05 moL/L NaCl+0.01 mol/L NaOH溶液中载波处理对纯镁耐蚀性能的影响.结果表明:载波处理后,纯镁表面生成了一层非常致密而细小的氧化膜,使表而更稳定,提高了纯镁的耐蚀性能.
参考文献
| [1] | Gray J E,Luan B.Protective coatings on magnesium and its alloys-a critical review[J].Journal of Alloys and Compounds,2002,336(1-2):88. |
| [2] | 宋光铃,曾楚南,林海潮,等.载波钝化及其后处理对不锈钢钝化膜组成及稳定性的影响[J].中国腐蚀与防护学报,1992,12(1):77. |
| [3] | 宋光铃,曹楚南,夏邦杰.等.电位及后处理对304不锈钢表面膜组成及稳定性的影响[J].金属学报,1992,28(8):369. |
| [4] | 宋光铃.镁合金腐蚀与防护[M].北京:化学工业出版社,2006.51. |
| [5] | Mansfeld F,Lin S H,Kwiatkowski L.The effects of process parameters on alternating voltage passivation of 304 stainless steel[J].Corros.Sci,1993,34(12):2045. |
| [6] | Igual Munoz A,Gareia Ant6n J,Guinon J L,et al.Inhibition effect of chromate on the possivation and pitting corrosion of a duplex stainless steel in LiBr solutions using electrochemical techniques[]].Corms.Sei,2007,49 (8):3200. |
| [7] | Blanco G,Bautista A,Takenouti H.EIS study of passivation of austenltie and duplex stainless steels reinforcements in simulated pore solutions[J].Cement & Concrete Composites,2006,28 (3):212. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%