采用循环伏安法在304不锈钢(304SS)基体上电化学合成聚吡咯(PPy)膜层,并通过Tafel极化曲线、电化学交流阻抗谱法(EIS)研究聚吡咯膜层的腐蚀防护性能.结果表明,聚吡咯膜层使304不锈钢基体的自腐蚀电位正移60 mV,腐蚀电流密度由10-6A/cm2变化到10-7A/cm2;覆有聚吡咯膜层的304不锈钢在腐蚀液中浸泡的过程中,由于聚吡咯的氧化还原能力,在金属表面加速钝化层的形成及修复破坏的钝化层,进一步提高了金属的抗腐蚀性能;聚吡咯膜层的防腐机制归结为物理屏蔽作用和钝化机制.
参考文献
[1] | 李永舫.导电聚合物[J].化学进展,2002,14(3):207. |
[2] | DeBerry D W.Modification of the Electrochemical and Corrosion Behavior of Stainless Steels With an Electroactive Coating[J].Electrochemical Society,1985,132:102. |
[3] | Wessling B.Passivation of metals by coating with polyanline:corrosion potential shift and morphological changes[J].Advanced Materials,1994,6:226. |
[4] | Talo A,Forsen O,Ylasaari S.Corrosion protective polyaniline epoxy blend coatings on mild steel[J].Synthetic Metals,1999,102:1394. |
[5] | Grgur B N,Gvozdenovic M M,Miakovic-Stankovic V B,et al.Corrosion behavior and thermal stability of electrodeposited PANI/epoxy coating system on mild steel in sodium chloride solution[J].Progress in Organic Coatings,2006,56:214. |
[6] | Taken T,Yazici B,Erbil M.The electrochemical synthesis and corrosion performance of polypyrrole on brass and copper[J].Progress in Organic Coatings,2004,51:152. |
[7] | Taken T,Ozyilmaz A T,Yazici B,et al.Polypyrrole and polyaniline top coats on nickel coated mild steel[J].Progress in Organic Coatings,2004,51:27. |
[8] | Tuken T.Polypyrrole films on stainless steel[J].Surface & Coatings Technology,2006,200:4.713. |
[9] | Grgur B N,Krstajic N V,Vojnovic M V,et al.The influence of polypyrrole films on the corrosion behavior of iron in acid sulfate solutions[J].Progress in Organic Coatings,1998,33:1. |
[10] | Lenz D M,Defamar M,Ferreira C A,et al.Application of polypyrrole/TiO2 composite films as corrosion protection of mild steel[J].Journal of Electroanalytienl Chemistry,2003,540:35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%