提出了镀锌钢板的稀土镧盐、硅烷协同钝化工艺,先在镀锌钢板表面沉积一层稀土镧盐转化膜,再用乙烯基三(B-甲氧基乙氧基)硅烷处理得到复合膜.盐雾试验、醋酸铅点滴试验、失重实验和电化学交流阻抗谱(EIS)测定表明,复合膜的耐蚀性优于单一镧盐转化膜和常规铬酸盐转化膜.扫描电镜(SEM)结果表明,复合膜表面极其致密均匀平整.漆膜划格试验结果表明,复合膜附着力达到5B标准,再涂装性可靠.
参考文献
| [1] | 王爱荣,郝海玲.常用镀锌层钝化工艺概述[J].电镀与精饰,2006,28(5):29. |
| [2] | 单凤君,刘常生,于晓中,等.镀锌钢板无铬钝化技术的研究进展[J].材料保护,2007,40(10):45. |
| [3] | 林碧兰,卢锦堂,孔纲.等.钼酸盐后处理提高热镀锌上磷化膜耐蚀性的探讨[J].腐蚀与防护,2007.28(8):396. |
| [4] | Dalbin S,Maurin G,Nogueira R P.Silica-based coating for corrosion protection of electrogalvanized steel[J].Surface &Comings Technology,2005,194 (2/3):363. |
| [5] | Dikinis V,Niaura G,Rezaite V,et al.Formation of conversion silicate films on Zn and their properties[J].Transactions of the Institute of Metal Finishing,2007,85 (2):87. |
| [6] | 胡会利,李宁,程瑾宁.镀锌植酸钝化膜耐蚀性的研究[J].电镀与环保,2005,25(6):21. |
| [7] | Bexell Ulf,Mikacl Grehk T.A corrosion study of hot-dip galvanized steel sheet pre-treated with γ-mercaptopropyltrimethoxysi-lane[J].Surface & Coatings Technology,2007,201 (8):4734. |
| [8] | 李鸿宾,陈建设,刘辉,等.热镀锌表面铈盐钝化[J].材料冶金学报.2002,1(3):203. |
| [9] | 杨柳,刘光明,钱余海.等.镀锌钢板铈盐钝化的电化学性能研究[J].表面技术,2006.35(6):11. |
| [10] | Ferreira M G S,Duarte R G,Montemor M F,et al.Silanes and rare earth salts as chromate replacers for pre-treatments on galvanised steel[J].Electrochimica Acta,2004,49(17/18):2927. |
| [11] | 吴海江,卢锦堂,孔纲.热镀锌钢表面铈盐与硅烷处理后的耐蚀性能[J].腐蚀与防护,2007.28(7):353. |
| [12] | 徐斌.满瑞林.倪网东,等.镀锌钢板表面硅烷、铈盐复合膜的制备及耐腐蚀性能研究[J].涂料工业,2007,37(12):46. |
| [13] | 卢燕平,任玉苓,邱明煊,等.电镀锌钢板涂敷型低铬钝化研究[J].表面技术,1998,27(2):9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%