综述了金属电化学腐蚀、应力腐蚀以及高温高压水环境下腐蚀过程中的声发射信号特征与产生机制,及目前研究现状与存在的问题,探讨了进一步研究的方向和思路.
参考文献
| [1] | 《国防科技工业无损检测人员资格鉴定与认证培训教材》编审委员会.声发射检测[M].北京:机械工业出版社,2005.1. |
| [2] | Retting T W,Felsen M J.Acoustic emission method for monitoring corrosion reactions[J].Corrosion,1976,32:121. |
| [3] | Mansfeld F,Stacker P J.Galvanic corrosion of Al alloys monitord by acoustic emission[J].Journal of the Electrochemical Society,1977,124:1301. |
| [4] | Mansfeld F,Stocker P J.Acoustic emission from corroding electrodes[J].Corrosion,1979,35:541. |
| [5] | Seal K H W,Lim K B,Chew C H,et al.The correlation of acoustic emission with rate of corrosion[J].Corrosion Science,1993,34:1707. |
| [6] | Kim Y P,Fregonese M,MaziUe H,et al.Ability of acoustic emission technique for detection and monitoring of crevice corrosion on 304L austenitic stainless steel[J].NlYr&E International.2003,36:553. |
| [7] | Mazille H,Rothea R,Tronel C.An acoustic emission technique for monitoring pitting corrosion of austenitic stainless steels[J].Corrosion Science,1995,37:1365. |
| [8] | Darowicki K,Mirakowski A,Krakowiak S.Investigation of pitting of stainless steel by means of acoustic emission and potentiodynamic methods[J].Corrosion Science,2003,45:1747. |
| [9] | Magaino S,Kawaguchi A,Hirata A.Spectrum analysis of corrosion potential fluctuations for localized corrogion of type 304 stainless steel[J].Journal of the Electrochemical Society,1987,134:2993. |
| [10] | Idrissi H,Ramadan S,Maghnouj J,et al.Modern concept of acoustic emission (AE) coupled with electrochemical measurements for monitoring the elastomer-coated carbon steel damage in phosphoric acid medium[J].Progress in Organic Coatings,2008,63:382. |
| [11] | Arora A.Acoustic emission characterization of corrosion reactions in aluminum alloys[J].Corrosion,1984,40:459. |
| [12] | Fregonese M,Idrissi H,Mazille H.Monitoring pitting corrosion of AISI 316L anstenitic stainless steel by acoustic emission technique:Choice of representative acoustic parameters[J].Journal of Materials Science,2001,36:557. |
| [13] | Fregonese M,Idrissi H,Mazille H,et al.Initiation and propogation steps in pitting corrosion of austenific stainless steels:monitoring by acoustic emission[J].Corrosion Science,2001,43:627. |
| [14] | Gorman M R.Plate wave acoustic emission[J].Journal of the Acoustical Society of America,1991,90:358. |
| [15] | Dunegan H L.Modal analysis of acoustic emission signals[J].Journal of Acoustic Emission,1998,15:1. |
| [16] | Chang H,Han E H,Wang J Q,et al.Analysis of modal acoustic emission signals of LY12CZ aluminum alloy at anedic and cathedic polarization[J].NDT&E International,2006,39:8. |
| [17] | 耿荣生,傅刚强.金属点蚀过程声发射源机制研究[J].声学学报.2002,27:369. |
| [18] | 张平,施克仁,耿荣生,等.小波变换在声发射检测中的应用[J].无损检测,2002,24:436. |
| [19] | 李伟.低碳钢点蚀声学检测与信号处理技术研究[D].大庆:大庆石油学院,2006.37. |
| [20] | 李伟,戴光,李宝玉.基于独立分量分析的金属腐蚀声发射信号处理[J].化工机械,2005,32:207. |
| [21] | 顾江,张光新,刘国华.等.基于独立分量分析的声发射信号去噪方法[J].江南大学学报,2008,7:55. |
| [22] | 易若翔,刘时风,耿荣生,等.人工神经网络在声发射检测中的应用[J].无损检测,2002,11:488. |
| [23] | Jones R H,Friesel M A.Acoustic emission during pitting and transgranular crack initiation in type 304 stainless steel[J].Corrosion,1992,48:751. |
| [24] | Kim Y P,Fregonese M,Mazille H,et al.Smdy of oxygen reduction on stainless steel surfaces and its contribution to acoustic emission recorded during corrosion processes[J].Corrosion Science,2006,48:3945. |
| [25] | Shaikh H,Amirthalingam R,Anita T,et al.Evaluation of stress corrosion cracking phenomenon in an AISI type 316LN stainless steel using acoustic emission technique[J].Corrosion Science,2007,49:740. |
| [26] | Okada H,Yukawa K,Tamura H.Application of acoustic emission technique to the study of stress corrosion cracking in distinguishing between active path corrosion and hydrogen embrittlement[J].Corrosion,1974,30:253. |
| [27] | Okada H,Yukawa K,Tamura H.Transition of cracking mechanism from active path corrosion to hydrogen embrittlement in high strength steels in a boiling nitrate solution[J].Corrosion,1976.32:201. |
| [28] | Ramadan S,Gaillet L,Tessier C,et al.Detection of stress corrosion cracking of high-strength steel used in prestressed concrete structures by acoustic emission technique[J].Applied Surface Science,2008,254:2255. |
| [29] | Kovac J,Leban M,Legat A.Detection of SCC on prestressing steel wire by the simultaneous use of electrochemical noise and acoustic emission measurements[J].Electrochimica Acts,2007,52:7607. |
| [30] | Jones R H,Friesel M A,Athania R.Evaluation of stress corrosion crack initiation using acoustic emission[J].Corrosion,1991,47:105. |
| [31] | Key Y S,In S K,Young K Y.Characteristic of acoustic emission during stress corrosion cracking of inconel 600 alloy[J].Scripts Materialia,1997,37:1255. |
| [32] | Gerberich W W,Jones R H,Friesel M A,et al.Acoustic emission monitoring of stress corrosion cracking[J].Materials Science and Engineering,1988,A103:185. |
| [33] | Jones R H,Friesel M A,Gerberich W W.Acoustic emission from intergranular suboritical crack growth[J].Metallurgical Transactions A,1989,20A:637. |
| [34] | Padmarmbhan R,Suriyayothin N.Wood W E.Grain size-acoustic emission relationships in hydrogen induced delayed cracking[J].Metallurgical Transactions A,1983,14A:2357. |
| [35] | Cakir A,Tuncell S,Alptekin A.AE response of 316L SS during SSR test under patentiustatic control[J].Corrosion Science,1999,41:1175. |
| [36] | Lapitz P,Ruzzante M G,Alvarez M G.AE response of α-brass during etress corrosion crack propagation[J].Corrosion Science,2007,49:3812. |
| [37] | Mvarez M G,Lapitz P,Ruzzante J.AE response of type 304 stainless steel during stress corrosion crack propagation[J].Corrosion Science,2008,50:3382. |
| [38] | Bennett M J,Buttle D J,Colledge P D,et al.SpaUation of oxide scales from 20% Cr-25Ni-Nb stainless steel[J].Materials Science and Engineering,1989,A120:199. |
| [39] | Li T F,Li M S,Guan H R.Critical cracking stress of oxide scales of tantalum due to oxidation[J].Materials Science and Engineering,1989,A120:235. |
| [40] | Li T F,Li M S.Influence of the parameters of oxidation process on the critical cracking stress of oxide scales of niobium and niobium alloy[J].Materials Science and Zngineering,1989,A120:239. |
| [41] | Jha B B,Baldev R,Khanna A S.Frequency analysis of AE signal obtained during breakaway oxidation and internal cracking of 2 Cr-1Mo steel at 900℃[J].Oxidation of Metals,1986,26:263. |
| [42] | Alekseev A B,Averin S A.Geferova M N,et al.Corrosion resistance of austenitic steels and alloys in high temperature water[J].Journal of Nuclear Materials 1996,233-237:1367. |
| [43] | Caasagne T,Caron D,Daret J,et al.Initial results on the stress corrosion cracking monitoring of alloy 600 in high temperature water using acoustic emission[A].Proceedings of Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors[C].Pennsylvania:The Minerals,Metals & Material Society,1999.225. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%