本文以3D针刺碳毡为增强体,热塑性酚醛树脂为先驱体,采用真空压力浸渍法多次浸渍一次碳化和一次浸渍一次碳化两种工艺制备碳/碳多孔预制体,以用于制备碳/碳化硅复合材料,研究真空度、增强体尺寸、浸渍液浓度、浸渍温度及压力等因素对浸渍效果的影响.结合试样碳化前后SEM显微结构变化,探讨了树脂液相浸渍机理.实验结果表明,树脂液相浸渍用真空度以稍高于浸渍液在浸渍温度下的饱和蒸气压为宜.树脂溶液浓度、浸渍温度和压力分别为80%、40～50 ℃和0.6 MPa时浸渍效果最好.增强体尺寸越大,浸渍效果越差.
参考文献
| [1] | S Vaidyaraman;M Purdy;T Walker;S Horst.C/SiC material evaluation for aircraft brake applications[A].,2001 |
| [2] | W Krenkel .Cost effective processing of composites by melt infiltration (LSI-Process)[J].Ceramic Engineering Science Proceedings,2001,22:442-444. |
| [3] | R Kochendorfer;N Lutzenburger.Application of CMCs made via the liquid silicon infiltration (LSI) technique[A].Meiheim:WILEY-VCH Verlag GmbH,2001 |
| [4] | M. Klucakova .Rheological properties of phenolic resin as a liquid matrix precursor for impregnation of carbon-carbon composites with respect to conditions of the densification process[J].Composites science and technology,2004(7/8):1041-1047. |
| [5] | 段永涛,张德翱.真空浸渍工艺的研究与应用[J].真空,2003(04):54-57. |
| [6] | 李晔;黄启忠;朱东波 等.液相浸渍法制备C/C复合材料[J].炭素科技,2002,12(03):38-40. |
| [7] | 陈惠钊.粘度测量[M].北京:中国计量出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%