本文研究了自制的CPP-g-GMA(氯化聚丙烯接枝甲基丙烯酸缩水甘油酯)对聚丙烯的粘接作用,并以CPP-g-GMA为底漆、双组分丙烯酸清漆为面漆对聚丙烯及其复合材料进行了涂装,探讨了CPP-g-GMA对涂层附着力的影响及其与接枝率的关系.结果表明,GMA的接枝可在一定程度上改善CPP与聚丙烯的粘接作用,能有效提高聚丙烯及其复合材料与丙烯酸漆的附着力,随着接枝率的增加,提高的幅度增大,在接枝率为2.31%时附着力等级可达到最高的0级.
In this paper, polypropylene (PP) bonding with CPP-g-GMA (glycidyl methacrylate grafted chlorinated polypropylene) was studied as well as bicomponent acrylic coating painted on PP and its composite after using CPP-g-GMA as a primer. The results show that the adhesive strength of CPP-g-GMA to PP is better to some extent than that of CPP to PP, and the adhesion strength of coating-substrate can be improved effectively. As the grafting degree of glycidyl methacrylate onto chlorinated increasing, the adhesion strength of coating-substrate increased more and more significantly. When using CPP-g-GMA with grafting degree of 2.31% as primer the coating adhesion can even reach class zero which is the best class.
参考文献
| [1] | 王秋峰,翟欢,侯静强,周晓东.熔体包覆法长玻璃纤维增强聚丙烯复合材料的力学性能[J].高分子材料科学与工程,2007(05):230-233. |
| [2] | 肖坤立,周晓东.热塑性复合材料的A级表面技术[J].纤维复合材料,2008(01):3-6. |
| [3] | Neitzel M;Blinzler M;Edehnann K et al.Surface Quality Characterication of Textile-Reinforced Thermoplastics[J].Polymer compoaites,2000,21:630-635. |
| [4] | 章益焱,周晓东,戴干策.聚丙烯材料粘结和涂装性能的改善方法[J].现代塑料加工应用,2004(04):60-64. |
| [5] | Tsuchiya Yasuyuki;Akutu Kensuke;Jwata Akinori.Surface modification of polymeric materials by atmospheric plasma troatment[J].Progress in organic Coatings,1998(34):100-107. |
| [6] | Horst H.B;Harald B .Coating of Untreated Polypropylene with Halogene Free Aqueous Materials[J].Progress in Organic Coatings,2000,40:49-54. |
| [7] | GB/T9286-1998.色漆和清漆漆膜的划格试验[S]. |
| [8] | 潘强余;吴教汉.高聚物的界面与粘合[M].北京:纺织工业出版社,1987 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%