石英/氮化物复合材料具有优异的综合性能,可用作高马赫数导弹天线罩材料.采用先驱体浸渍裂解法制备的该复合材料存在易吸潮的缺点,吸潮后会影响其透波性能.研究制备了复合材料的聚偏氟乙烯(PVDF)涂层.测试发现,聚偏氟乙烯(PVDF)涂层具有优良的防潮性能,在40℃、90%高温高湿条件下放置70d的增重率为0.934%.PVDF涂层对复合材料的透波性能影响较小,涂覆厚度约300μm的涂层前后介电常数及介电损耗分别为3.48、0.0051和3.62、0.0053.
参考文献
| [1] | 齐共金,张长瑞,胡海峰,曹峰,王思青,曹英斌,姜勇刚.陶瓷基复合材料天线罩制备工艺进展[J].硅酸盐学报,2005(05):632-638. |
| [2] | 张大海,黎义,高文,陈英,方超.高温天线罩材料研究进展[J].宇航材料工艺,2001(06):1-3. |
| [3] | Barta J;Manela M;Fischer R.Si3N4 and Si2N2O for high performance radomes[J].Materials Science and Engineering,1985(71):265-272. |
| [4] | Morozumi H;Sato K;Tezuka A.Preparation of high strength ceramic fiber reinforced silicon nitride composites by a preceramic polymer impregnation method[J].Ceramics International,1997(23):179-184. |
| [5] | H. Chen;L. M. Zhang;G. Y. Jia;W. H. Luo;S. Yu .The Preparation and Characterization of 3D-Silica Fiber Reinforced Silica Composites[J].Key engineering materials,2003(249):159-162. |
| [6] | Semff L.R .High yield-low carbon ceramic via siliconbased polymers[P].US:5948348,1999-07-07. |
| [7] | Semff L.R .Method for making high yield-low carbon ceramic via polysilazane[P].US:6063327,2000-06-17. |
| [8] | 陈虹,胡利明,贾光耀,齐健梅,邹秀娟,张联盟.陶瓷天线罩材料的研究进展[J].硅酸盐通报,2002(04):40-44. |
| [9] | 苏震宇,周洪飞.天线罩用耐高温复合材料的研究[J].玻璃钢/复合材料,2005(06):35-37. |
| [10] | 舒卫国,杨博.大尺寸高性能雷达天线罩的研制[J].玻璃钢/复合材料,2006(01):51-52,44. |
| [11] | 王维,刘永琪,张小兵,刘芳芳,敬辉.纤维增强树脂基复合材料透波板的研制和试验[J].玻璃钢/复合材料,2008(02):26-29. |
| [12] | 姜卫陵,郦江涛,赵云峰,罗萍,李德利.聚四氟乙烯透波罩软模成型工艺及材料性能研究[J].宇航材料工艺,2002(01):46-49. |
| [13] | 曾剑平;黎义;吴远秀.有机硅树脂在SiO2基复合材料中的应用[J].宇航材料工艺,1997(03):26-31. |
| [14] | 包宁;林彬 .天线罩表面涂层的研究[J].航天制造技术,2004,24(05):553-557. |
| [15] | 管丛胜;王威强.氟树脂涂料及应用[M].北京:化学工业出版社,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%