微胶囊二元自修复系统对聚合物基复合材料在使用中产生的微小裂纹具有修复作用,但微胶囊和固化剂的加入会对基体材料的断裂韧性产生影响.本文研究了环氧树脂微胶囊和咪唑类潜伏性固化剂对聚合物基复合材料基体材料的断裂韧性的影响.采用环氧树脂E-51作为基体材料,三乙烯四胺为常温固化剂,咪唑类衍生物2MZ-Azine和实验室自制的包含环氧树脂芯材的微胶囊为材料制作断裂韧性拉伸试样.实验结果表明,当微胶囊的含量达到一定比例之前,基体材料的断裂韧性随着微胶囊含量的增加而增强,当微胶囊含量超过此比例后,基体材料的断裂韧性随着微胶囊含量的增加而减小,潜伏性固化剂的加入会增大基体材料的断裂韧性.这与环氧树脂材料增韧理论相符合.
参考文献
| [1] | 乔吉超,胡小玲,管萍.自修复聚合物材料用微胶囊的研究进展[J].化工进展,2006(12):1405-1409,1414. |
| [2] | Li Victor C;Lim Yun Mook;Chan Yin Wen .Feasibility study of a passive smart self-healing cementitious composite[J].Composites Part B:Engineering,1998,29(06):819-827. |
| [3] | 李海燕,王荣国,刘文博,郝焕英.微胶囊自修复复合材料的研究进展[J].玻璃钢/复合材料,2007(04):48-52. |
| [4] | S.R.White;N.R.Sottos.Autonomic Healing of Polymer Composite[J].Nature,2001(409):794-797. |
| [5] | 袁彦超,容敏智,章明秋.三聚氰胺-甲醛树脂包裹环氧树脂微胶囊的制备及表征[J].高分子学报,2008(05):472-480. |
| [6] | Yuan L;Liang GZ;Xie JQ;Li L;Guo J .Preparation and characterization of poly(urea-formaldehyde) microcapsules filled with epoxy resins[J].Polymer: The International Journal for the Science and Technology of Polymers,2006(15):5338-5349. |
| [7] | Haiyan Li;Rongguo Wang;Honglin Hu;Wenbo Liu .Surface Modification Of Self-healing Poly(urea-formaldehyde) Microcapsules Using Silane-coupling Agent[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2008(5P1):1894-1900. |
| [8] | Wang, RG;Li, HY;Hu, HL;He, XD;Liu, WB .Preparation and Characterization of Self-Healing Microcapsules with Poly(urea-formaldehyde) Grafted Epoxy Functional Group Shell[J].Journal of Applied Polymer Science,2009(3):1501-1506. |
| [9] | 党旭丹 .微胶囊自修复复合材料断裂力学实验研究[D].郑州大学,2005. |
| [10] | 柴红梅,汪鹏,王雷,孙超明,薛忠民,李鹏.固化剂含量对RTM用环氧树脂体系固化性能的影响[J].玻璃钢/复合材料,2009(06):48-49,76. |
| [11] | 李海燕,王荣国,刘文博,胡宏林.微胶囊自修复聚合物材料[J].宇航材料工艺,2010(01):1-4,13. |
| [12] | 杨艳娟,张恒,张军,王双华,段成金,贺跃进.微胶囊自修复复合材料断裂力学实验研究[J].材料导报,2007(01):143-144,147. |
| [13] | 王晓洁,谢群炜,张炜,尤丽虹.环氧树脂基体固化研究[J].玻璃钢/复合材料,2001(02):10-12. |
| [14] | E.N.Brown;N.R.Sottos.Performance of Embedded Microspheres for Self-Healing Polymer Composites[J].Society of Experimental Mechanical International Congress on Experimental Mechanics,2000:563-566. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%