为了揭示T700/5224复合材料在真空热循环作用下的力学性能演化规律,本文在10 -5Pa,- 140～140℃条件下,对T700/5224复合材料的质损率和力学性能进行了表征,并采用SEM分析方法对试样表面形貌、断口特征及表层化学结构进行了研究.研究结果表明,随真空热循环次数的增加,T700/5224复合材料的质损率升高,经29次真空热循环后上升幅度降低,而经157次真空热循环后趋于平缓.随着真空热循环次数的增加,T700/5224复合材料90°拉伸强度首先降低,48次热循环后开始升高,198次热循环后趋于平缓；弯曲强度在48次真空热循环前变化不明显,48次真空热循环后开始上升,95次真空热循环后开始降低,经198次真空热循环后趋于平缓；层剪强度变化不明显.
参考文献
| [1] | 柯受全.卫星环境工程和模拟试验(下)[M].北京:宇航出版社,1996:283-295. |
| [2] | 王浚;黄本诚;万大才.环境模拟技术[M].北京:国防工业出版社,1996:195-200. |
| [3] | G.Ambrosi.AMS,a Partical Detector in Space:Result from the precursor Flight and Status of AMS-02[J].Nuclear Physics B,2003(125):236-244. |
| [4] | R. Walker;C. E. Martin .Cost-effective and robust mitigation of space debris in low earth orbit[J].Advances in Space Research: The Official Journal of the Committee on Space Research(COSPAR),2004(5):1233-1240. |
| [5] | Koji Fujimoto;Tadashi Shioya;Katsuhiko Satoh .Degradation of carbon-based materials due to impact of high-energy atomic oxygen[J].International journal of impact engineering,2003(1):1-11. |
| [6] | 朱光武,李保权.空间环境对航天器的影响及其对策研究[J].上海航天,2002(04):1-7. |
| [7] | 王玉林,万怡灶,陈桂才,周福刚,成国祥.三维编织碳纤维/环氧复合材料的吸湿特性及外应力的影响[J].复合材料学报,2002(06):101-105. |
| [8] | 宋伟,齐俊伟,肖军,罗鹏.碳纤维/环氧预浸料的热固化工艺研究[J].玻璃钢1复合材料,2011(01):48-51. |
| [9] | 乌云其其格,廖子龙,李明.3233树脂及其复合材料性能研究[J].玻璃钢/复合材料,2003(06):16-18. |
| [10] | 王平,张条兰,罗永康,温月芳,杨永岗.层错结构对玻璃纤维/炭纤维混杂复合材料弯曲性能的影响[J].玻璃钢/复合材料,2010(04):57-61. |
| [11] | 习年生,于志成,陶春虎.纤维增强复合材料的损伤特征及失效分析方法[J].航空材料学报,2000(02):55-63. |
| [12] | Heinrich JABS .Effect of Space Exposure of Some Epoxy Matrix Compositeson Their Thermal Expansion and Mechanical Property[NNASA N92-24844][R]. |
| [13] | 高禹;杨德庄;何世禹 .真空热循环对M4OJ/环氧复合材料力学性能的影响[J].材料研究学报,200,18(05):529-536. |
| [14] | 高禹,李志君,杨德庄,何世禹,覃耀春.真空热循环对单向M40J/5228A复合材料质损率和线膨胀系数的影响[J].复合材料学报,2004(06):108-113. |
| [15] | 吴运学;王晓薇;张涛 等.碳化硅/铝复合材料热循环损伤的初步研究[J].宇航材料工艺,1992,22(04):62-66. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%