对燃烧还原化合法制备氮化钛粉末的过程进行了理论分析.热力学计算结果表明,与只用镁还原的方案相比,在氮气环境中采用镁加碳联合还原的方案可获得含氧量很低的合成产物.氮化钛还原化合的最佳理论反应温度为1563～1893K.动力学分析结果表明,制备氮化钛时存在高氮压临界条件,原因在于需要克服压坯渗透能垒,而在反应物中添加少量的含氮化合物可有效降低这一临界数值.
参考文献
| [1] | Subrahmam J;Vijayakumar M .Self-propagating high-temperature synthesis[J].Journal of Materials Science,1992,27(06):6249-6273. |
| [2] | Munir Z A;Holt J B .Synthesis of high temperature materials by self-propagating combustion methods[J].American Ceramic Society Bulletin,1988,67(02):342-349. |
| [3] | Merzhanov A G.Self-propagating high-temperature synthesis: twenty years of search and findings, in combustion and plasma synthesis of high temperature materials[M].New York:VCH,1990 |
| [4] | 莫畏.钛冶金[M].北京:冶金工业出版社,1979 |
| [5] | Wang L L;Munir Z A;Maximov Y M .Thermite reaction : their utilization in the synthesis and processing of materials[J].Journal of Materials Science,1993,28(04):3693-3708. |
| [6] | 吉林工业大学;吉林工学院.物理化学[M].北京:机械工业出版社,1980 |
| [7] | 印永嘉.物理化学简明手册[M].北京:高等教育出版社,1988 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%