研究了La3+取代的(Bi1.5Zn0.5)(Ti1.5Nb0.5)O7基陶瓷(Bi1.5-xLaxZn0.5)(Ti1.5Nb0.5)O7(0.0≤x≤1.2,BLZNT)的结构与介电性能.采用传统的固相反应法制备了陶瓷样品,用XRD、SEM分析了样品的组织.在整个取代范围内,La3+取代的样品基本保持单一烧绿石相,稳定范围由容忍因子(RA/RB值)来确定;同时,随着La3+取代量的增加,晶胞常数先增后减.介电性能随结构变化而变化,其中介电性能为:ε=130~170,tanδ= ~0.9×10-3(1MHz),并且掺杂La优化了BLZNT-x样品高频端(>100 kHz)的频谱特性.
参考文献
[1] | M. Valant;P. K. Davies .Synthesis and dielectric properties of pyrochlore solid solutions in the Bi2O3-ZnO-Nb2O5-TiO2 system[J].Journal of Materials Science,1999(22):5437-5442. |
[2] | Davies;Valant P K .Crytal chemistry and dielectric properties of chemically substituted (Bi1.5Zn1.0Nb1.5)O7 and Bi2(Zn2/3Nb4/3)O7 pyrochlores[J].Journal of the American Ceramic Society,2000,83(01):147-153. |
[3] | MERGEN A;Lee W E .Crystal chemistry,thermal expansion and dielectric properties of (Bi1.5Zn0.5)(Sb1.5Zn0.5)O7 pyrochlore[J].Materials Research Bulletin,1997,32:175-189. |
[4] | 汪宏,张德生,王晓莉,姚熹.La3+取代Bi3+的 Bi2O3-ZnO-Nb2O5基陶瓷的结构与介电性能[J].硅酸盐学报,1998(04):532-536. |
[5] | Subramanion M A;Aravamudan G;SubbaRao G V .Oxide pyrohlores-a review[J].Progress in Solid State Chemistry,1983,15:55-143. |
[6] | Hannon R D .Dielectric polarizabilities of ions in oxides and fluorides[J].Journal of Applied Physics,1993,73(01):348-366. |
[7] | Champarnaud-Mesjard C;Maniet M;Frit B et al.Bismuth(Ⅲ)-and antimony(Ⅴ)-based ceramics with anion-deficient fluorite structure[J].Journal of Alloys and Compounds,1992,188:174-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%