用光学显微镜、扫描电镜、电子耗散能谱和X射线衍射仪研究了电磁搅拌对富Ce混合稀土(MM)合金化AZ91D镁合金组织和结构的影响.结果表明,随富Ce混合稀土加入量的增加,初生相细化,β相(Mg17Al12)的相对量降低,尺寸减小,由连续网状向分离的球粒状转变.形成的Al11MM3化合物数量增多,由主要以短棒状在晶内和晶界分布向大的针状在晶界分布过渡,甚至在晶界成簇聚集.强电磁搅拌作用下,随等温搅拌温度降低,初生相尺寸变小,其形貌由球粒状加少量的玫瑰状向类球状和多边形演变;A11MM3以类球状和细小的针状分布于晶粒和液相中.富Ce混合稀土可显著细化晶粒,改善β相的形貌和分布,降低体积分数;改变富Ce混合稀土含量可控制Al11MM3化合物的形貌和分布.电磁搅拌可同时使初生相和第二相Al11MM3细化和球粒化.
参考文献
| [1] | Ifeanyi A. Anyanwu;Yasuhiro Gokan;Atsuya Suzuki .Effect of substituting cerium-rich mischmetal with lanthanum on high temperature properties of die-cast Mg-Zn-Al-Ca-RE alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):93-99. |
| [2] | Polmesr I J .Magnesium alloys and applications[J].Materials Science and Technology,1994,10(01):1-16. |
| [3] | Luo A;Pekguleryuz MO.Cast magnesium alloys for elevated temperature applications[J].Journal of Materials Science,1994(29):5259-5271. |
| [4] | Mordike B L;Ebert T .Magnesium:properties applications potential[J].Materials Science and Engineering,2001,302:37-45. |
| [5] | 王立世,段汉桥,魏伯康,张诗昌.混合稀土对AZ91镁合金组织和性能的影响[J].特种铸造及有色合金,2002(03):12-14. |
| [6] | 张诗昌,魏伯康,陈渭臣.钇及混合稀土对AZ91镁合金流动性与凝固组织的影响[J].铸造,2004(02):118-121. |
| [7] | Spigarelli S;Regev M et al.Review of creep behaviour of AZ91 magnesium ally produced by different technologies[J].Materials Science and Technology,2001,17:627-638. |
| [8] | 王晓虎,赵爱民,毛卫民,甄子胜.电磁搅拌下金属流体的流场测量与研究[J].特种铸造及有色合金,2003(02):47-49. |
| [9] | H. V. Atkinson .Modelling the semisolid processing of metallic alloys[J].Progress in materials science,2005(3):341-412. |
| [10] | 李子全;吴炳尧;于平.等温温度和微量合金化对电磁搅拌ZA-27流变组织的影响[J].铸造,1997(12):6-11. |
| [11] | 王渠东,吕宜振,曾小勤,丁文江,朱燕萍.稀土在铸造镁合金中的应用[J].特种铸造及有色合金,1999(01):40-43. |
| [12] | Lu Yizhen;Wang Qudong;Zeng Xiaoqin.Effects of rare earths on the microstructure,properties and fracture behavior of Mg-Al alloys[J].Materials Science and Engineering A,2000(278):66-67. |
| [13] | M C Flemings .Behavior of Metal Alloys in the Semisolid State[J].Metallurgical and Materials Transactions,1991,22B(06):269-293. |
| [14] | 王强,王春江,王恩刚,赫冀成,高桥弘纪,渡辺和雄.强磁场对不同磁化率非磁性金属凝固组织的影响[J].金属学报,2005(02):128-132. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%