研究了AZ31B镁合金轧板经不同温度、时间退火后的组织和性能及其再结晶行为.结果表明,热轧板材在退火过程中主要发生再结晶;退火后,强度略有下降,但伸长率明显提高;在523K下退火,保温60min,可获得平均晶粒直径为10 μm的细晶组织,其抗拉强度为258MPa,断裂伸长率为22.3%,综合性能较好.热轧态板材呈脆性准解理断裂,退火后转变为韧性断裂.
参考文献
| [1] | Yamashita A;Horita Z;Langdon T G .Improving the mechanical of magnesium and magnesium alloy through severe plastic deformation[J].Y Mater Sci Eng A,2001,A300:142. |
| [2] | Mukai T;Yamanoi M;Watanabe H et al.Ductility enhancement in AZ31 magnesium alloy by controlling its grain structure[J].Scripta Materialia,2001,45:89. |
| [3] | 马洪涛,杨蕴林,张柏清,方鸿生.MB26合金的静态与动态再结晶[J].金属热处理,1999(02):12-13. |
| [4] | Tan J C;Tan M J .Superplasticity and grain boundary sliding characteristics in two stage deformation of Mg3Al-Zn alloy sheet[J].Materials Science and Engineering,2003,A339:81-89. |
| [5] | 陈振华.变形镁合金[M].北京:化学工业出版社,2005 |
| [6] | 范永革,汪凌云,黄光胜,黄光杰,卢志文.变形镁合金板材在退火时的组织演变[C].2002年材料科学与工程新进展（2002年中国材料研讨会：论文专辑）,2002:675-678. |
| [7] | Avedesian M M;Baker H.ASM Specialty Handbook-Magnesium and Magnesium Alloys[M].ASM International,1999 |
| [8] | Mamoru Mabuchi;Masaaki Kobata;Yasumasa Chino .Tensile Properties of Directionally Solidified AZ91 Mg Alloy[J].Materials transactions,2003(4):436-439. |
| [9] | 林英男 .AZ31镁合金晶粒细化及成形性研究[D].台北:国立中央大学,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%