为增加(SiC)P与金属基体间的润湿性,采用化学镀方法对(SiC)P进行了低成本的表面涂覆改性,得到全包覆的改性(Ni/SiC)P ,以其为第二相粒子制备出Ni-P-(Ni/SiC)P化学复合镀层,观测了该镀层的形貌、成分及厚度,并与常见的Ni-P化学镀层、Ni-P-(SiC)P化学复合镀层比较.结果显示:Ni-P-(Ni/SiC)P镀层组织均匀、沉积量大,镀层厚度明显增加.
参考文献
[1] | Y. -F. Lee;S. -L. Lee;C. -L. Chuang;J. -C. Lin .Effects of SiC{sub}p reinforcement by electroless copper plating on properties o Cu/SiC{sub}p composites[J].Powder Metallurgy,1999(2):147-152. |
[2] | S. H. Hsieh;T. J. Yang .Study of the Composite Coating of SiC Particles Dispersed in an Electroless Nickel Matrix[J].Key engineering materials,2003(249):195-198. |
[3] | Grosjean A.;Takadoum J.;Bercot P.;Rezrazi M. .Hardness, friction and wear characteristics of nickel-SiC electroless composite deposits[J].Surface & Coatings Technology,2001(1):92-96. |
[4] | Hojo junichi;Hong Fumio;Kuga Tatsuhiko .Metal and carbide coatings of ceramics particles using chemical plating techniques[J].Journal of the Japan Society of Powder and Powder Metallurgy,1993,40(12):1185-1189. |
[5] | Y.C.Wu;G.H.Li .WEAR RESISTANCE OF ELECTROLESS DEPOSITED Ni-P AND Ni-P/SiC COMPOSITE COATINGS ON LOW ALLOY CAST IRON[J].Surface Engineering,2000(6):506-510. |
[6] | 余新泉,沈承芬.化学沉积法制备Ni-P-SiC(C)复合镀层的研究[J].东南大学学报(自然科学版),2002(02):245-248. |
[7] | Leonca H E;Drewral J M.Preparation of nickel coated powders as precursors to reinforce[J].Materials Science,2000(35):4763-4768. |
[8] | 宿辉,曹茂盛,王正平,邹桂真.SiC颗粒的表面修饰及结构表征[J].材料工程,2005(02):37-40. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%