利用电化学阳极氧化的方法,在草酸溶液中,精确控制反应条件,在高纯铝片表面有序生长了纳米多孔氧化铝膜.试验中,分别采用一次阳极氧化和二次阳极氧化方法制备氧化铝膜.利用H3PO4溶液浸泡法对氧化铝膜进行扩孔处理.通过扫描电子显微镜对样品进行表征分析.结果发现,二次阳极氧化制备的氧化铝膜的孔洞分布较一次氧化的更为规则有序,并且孔径大小均匀一致.扫描电镜观察显示,氧化铝膜的扩孔过程可以去掉阻碍层,并调节孔径大小,溶去二次氧化后黏附在氧化层表面的一些杂质,从而使氧化铝模板更为规则有序,孔径均一.这种经过二次阳极氧化和扩孔处理得到多孔阳极氧化铝模板的方法简单,成本较低,可以为后续的纳米材料合成提供高质量的合成模板.
参考文献
| [1] | 王鸿建.电镀工艺学[M].哈尔滨:哈尔滨工业大学出版社,1988:177-193. |
| [2] | Treverton J A;Ball J;Johnson D et al.SSIMS,XPS and microstructural studies of ac phosphoric acid anodic films on aluminium[J].Surface and Interface Analysis,1990,16:369. |
| [3] | Hernandez A.;Martin A.;Pradanos P.;Martinez F. .POROUS STRUCTURE AND SURFACE CHARGE DENSITY ON THE WALLS OF MICROPOROUS ALUMINA MEMBRANES[J].Journal of Colloid and Interface Science,1995(2):284-296. |
| [4] | Martin C R;Vandyke L S;Cai Z H .Template synthe-sis-a method for enhancing the ionic and electronic conductivity in electronically conductive polymers[J].Electrochimica Acta,1992,37(09):1611-1613. |
| [5] | 于冬亮,杨绍光,朱浩,都有为.钴纳米线阵列的制备和磁性[J].南京工业大学学报(自然科学版),2000(06):69-71. |
| [6] | 郭云,覃东欢,力虎林.Fe0.3Co0.7纳米有序阵列的制备及磁学特性[J].兰州大学学报（自然科学版）,2005(04):56-59. |
| [7] | 潘善林,张浩力,彭勇,王臻,力虎林.模板合成法制备金纳米线的研究[J].高等学校化学学报,1999(10):1622-1624. |
| [8] | 朱泓,黄新民.氧化铝模板制备ZnO纳米有序阵列及其光致发光性能研究[J].纳米科技,2005(02):37-39. |
| [9] | 王爱华,管荻华,周维亚,王刚,解思深.多孔氧化铝有序膜的制备研究[J].无机化学学报,2002(05):447-450. |
| [10] | 张立德;牟季美.纳米材料和纳米结构[M].北京:科学出版社,2001:118-133. |
| [11] | 马春兰.高质量规则多孔氧化铝模板的制备[J].物理学报,2004(06):1952-1955. |
| [12] | Xue F H;Fei G T;Wu B et al.Direct electrodeposition of highly dense Bi/Sb superlattice nanowire arrays[J].Journal of the American Chemical Society,2005,127:15348. |
| [13] | Masuda H;Fukuda K .ORDERED METAL NANOHOLE ARRAYS MADE BY A TWO-STEP REPLICATION OF HONEYCOMB STRUCTURES OF ANODIC ALUMINA[J].Science,1995(5216):1466-1468. |
| [14] | Hideki Masuda;Hidetaka Asoh;Mitsuo Watanabe;Kazuyuki Nishio;Masashi Nakao;Toshiaki Tamamura .Square and Triangular Nanohole Array Architectures in Anodic Alumina[J].Advanced Materials,2001(3):189-192. |
| [15] | Parkhutik V P;Shershulsky V I .Theoretical modeling of porous oxide growth on aluminum[J].Journal of Physics D:Applied Physics,1992,25:1258-1263. |
| [16] | Xu Y;Thompson G E;Wood G C .Mechanism of anodic film formation on aluminium[J].Transactions of the Institute of Metal Finishing,1985,63:98-103. |
| [17] | Jessensky O.;Gosele U.;Muller F. .Self-organized formation of hexagonal pore arrays in anodic alumina[J].Applied physics letters,1998(10):1173-1175. |
| [18] | 江小雪,赵乃勤.多孔氧化铝膜的制备与形成机理的研究概况[J].功能材料,2005(04):487-489,494. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%