针对1Cr17铁素体不锈钢冲击制品硬度随冲击载荷变化增加的情况,进行了一定的实验研究,分析了1Cr17铁素体不锈钢在激光冲击下的组织变化机理,结果表明,随着激光功率增加,1Cr17的加工硬化效应相应提高,得到的硬度越高;在激光冲击后,铁素体的组织主要以调幅分解为主,激光功率增加,调幅分解加剧,形成的格子布形态粗化,并最终在激光功率42J的冲击过程中导致相变产生,生成类马氏体组织.
参考文献
| [1] | 李晓波.国内铁素体不锈钢的最新发展[J].铸造设备研究,2006(04):52-54. |
| [2] | S Charles;Montross;Tao Wei.Laser shock processing and its effects on microstructuer and properties of metal alloys:a Review[J].International Journal of Fatigue,2002(24):1021-1036. |
| [3] | 马壮,李应红,张永康,任旭东,张凌峰.激光冲击处理对304不锈钢力学性能的影响[J].材料热处理学报,2007(03):102-105. |
| [4] | Y. K. Zhang;X. R. Zhang;X. D. Wang;S. Y. Zhang;C. Y. Gao;J. Z. Zhou;J. C. Yang;L. Cai .Elastic properties modification in aluminum alloy induced by laser-shock processing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):138-143. |
| [5] | Kotoji Ando;Hirohito Eto;Katsuyuki Matsui .Influence of retained austenite,strain-induced martensite and bending stress upon shot peening-induced residual compressive stresses[J].Trans of Japan Society of Mechanical Engineers,2002,68(07):1947-1958. |
| [6] | 王六定,陈长乐,卫英慧,康沫狂.面心立方合金调幅分解与有序化的X射线和透射电镜衍射研究[J].航空材料学报,1999(03):13-18. |
| [7] | 周建忠,张永康,周明,殷苏民,杨继昌,吴鸿兴,郭大浩.单次激光冲击下板料变形的理论分析[J].中国激光,2005(01):135-138. |
| [8] | 周建忠 .金属板料激光冲击成型加载机制及变形特性研究[D].镇江:江苏大学,2003. |
| [9] | 李晓轩,孙锡军,王华明,邹世坤,王健.奥氏体不锈钢1Cr18Ni9Ti激光冲击强化研究[J].宇航材料工艺,1999(04):16-19. |
| [10] | Clauer A H;Walters C T;Ford S C.Analysis of the precipitation process of the intermetallic phases in Fe-Ni alloy[A].EACD Ohio,1983:1021-1032. |
| [11] | 许淳淳,张新生,胡钢,王东,雒娅楠.不锈钢冷加工形变诱发马氏体相变及其腐蚀行为[J].材料保护,2002(03):15-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%