研究了挤压态Mg-10Gd-3Y合金的动态维氏硬度,分析了压痕周围的微观组织,并与静态维氏硬度值进行对比.结果表明:挤压态Mg-10Gd-3Y合金动态维氏硬度高于静态维氏硬度,表现出明显的应变率正效应,并且其动态维氏硬度随应变量的增加出现一个极大值,压痕周围出现孪晶组织,随应变量的增加孪晶数量减少.
参考文献
| [1] | Wei Qian Song;Peter Beggs;Mark Easton .Compressive Strain-rate Sensitivity Of Magnesium-aluminum Die Casting Alloys[J].Materials & design,2009(3):642-648. |
| [2] | E. El-Magd;M. Abouridouane .Characterization, modelling and simulation of deformation and fracture behaviour of the light-weight wrought alloys under high strain rate loading[J].International journal of impact engineering,2006(5):741-758. |
| [3] | Richard J. Anton;Ghatu Subhash .Dynamic Vickers indentation of brittle materials[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2000(1):27-35. |
| [4] | B. J. Koeppel;G. Subhash .Characteristics of residual plastic zone under static and dynamic Vickers indentations[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(1):56-67. |
| [5] | 余继军 .单晶硅材料动态压痕试验系统的建立及试验研究[D].哈尔滨工业大学,2006. |
| [6] | 周海涛,曾小勤,刘文法,丁文江,朱燕萍.稀土铈对AZ61变形镁合金组织和力学性能的影响[J].中国有色金属学报,2004(01):99-104. |
| [7] | Mathis K;Trojanova Z;Lukac P et al.[J].Journal of Alloys and Compounds,2004,378:176. |
| [8] | Klimanel P;Potzsch A .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2002,324:145. |
| [9] | 张新明,彭卓凯,邓运来,陈健美,蒋浩.Mg-9Gd-4Y-0.6Mn合金在293～723 K时的变形行为及微观组织演变[J].中南大学学报（自然科学版）,2006(02):223-228. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%