综述了超细WC-Co硬质合金的组织与性能特征.超细硬质合金因其粉末原料细小,比表面积特别大,易氧化,含氧量高,氧在还原过程中对碳平衡产生了显著的影响,使碳含量的控制显得尤为重要.随着超细硬质合金粉末原料的细化,合金需要达到完全致密的烧结温度就越低.晶粒长大抑制剂的加入使超细硬质合金的收缩率曲线开始收缩温度相对要低,且收缩峰变宽;并且它对超细硬质合金的性能和组织产生重大的影响.超细硬质合金具有普通硬质合金难以达到的高硬度和强度,以及比同类普通硬质合金的高得多的矫顽磁力.

参考文献

[1] 张卫兵.WC、Co质量对超细硬质合金性能影响的研究[J].硬质合金,2003(03):157-160.
[2] 株洲硬质合金厂.硬质合金生产[M].,1974:251-252.
[3] Uhrenius B.Phase equilibria and the sintering of cemented carbides[A].Paris,1994:1443-50.
[4] Silana Luyckx;Mohamed Zunaid A1li .Comparison between VC and Cr3C2 as grain refiners for WC-Co[J].Materials & Design,2001,22:507-510.
[5] S. Lay;S. Hamar-Thibault;A. Lackner .Location of VC in VC, Cr_3C_2 codoped WC-Co cermets by HREM and EELS[J].International Journal of Refractory Metals & Hard Materials,2002(1):61-69.
[6] 刘寿荣;周金亭 .TaC、Cr3C2对WC-Co硬质合金组织和性能的影响[J].硬质合金,1997,14(01):22.
[7] Silana Luyckx;Mohamed Zunaid Alli 等.Comparison between VC and Cr3C2 as grain refiners for WC-Co[J].Materials & Design,2001,22:507-510.
[8] 吴恩熙,雷贻文.超细硬质合金中晶粒生长抑制剂的作用[J].硬质合金,2002(03):136-139.
[9] Almond EA;Roebuck B.Origin of WC substructure and effect of processing on microstructure of WC/Co Hard metals[A].,1981:659-79.
[10] Kumazawa M .Mechanism of crystal growth and coalescence of WC in presence of liquid Co phase[J].Materials Transactions,1990,31:685-8.
[11] Suzuki T;Shibuki K;Suzuki T;Ikuhara Y .Grain boundary in cemented carbides[J].Philosophical Magazine Letters,1995,5:289-92.
[12] KimJD;Lay S;Allibert CH.WC crystal features in WC powder and in WC-Co mixtures along sintering[A].,1999:293-300.
[13] Warren R;Waldron MB .Microstructural development during liquid phase sintering of cemented carbides Ⅰ wettability and grain contact,Ⅱ carbide grain growth[J].Powder Metallurgy,1972,15:166-201.
[14] Roure S.Densification de malanges de poudres WC-Co:de lacompression au frittage[M].Doctorate Thesis,Institut Polytechnique de Grenoble,France,1996
[15] 美国金属学会.硬质合金工具的破损及其断裂韧性[M].北京:冶金工业出版社,1989:224-239.
[16] 陈楚轩 .硬质合金生产过程中的质量控制[Z].
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%