为探究Mo、WC、ZrC对TiC-Ni系金属陶瓷组织的影响,真空烧结制备了TiC-Ni系金属陶瓷.利用X射线衍射仪(X-ray diffraction,XRD)、扫描电子显微镜(scanning electron microscope,SEM)、能谱仪(energy dispersive spectrometer,EDS)等研究了Mo、WC和ZrC对金属陶瓷显微组织的影响.结果表明,TiC基金属陶瓷的显微组织随着Mo、WC、ZrC的加入而逐渐细化.形成(Ti,Mo)C、(Ti,Zr,Mo)C、(Ti,Mo,W)C、(Ti,Zr,Mo,W)C、(Zr,Yi,Mo)C和(Zr,Ti,Mo,W)C等固溶体,并且在10%TiC-ZrC-14%Mo-15%WC-20%Ni-1%C试样中出现了无芯晶粒(corelesss grains)、微裂纹及微孔洞.断裂韧性测试结果表明.该显微结构能大大提高材料的断裂韧性.

参考文献

[1] Kwom W T;Park J S;Kim SW;et el .Effect of WC and group IV carbides on the cutting performance of Ti(C,N)ceamet tools[J].lnt J Mach tools & Vamu,2004,944:341-346.
[2] gwoa W T;Park J S;Kang S et al.Effect of group IV dements on the catting cbaracteristics of Ti(C,N)cermet tools and rdiability analysis[J].Journal of Materials Processing Technology,2005,166:9-14.
[3] 章晓波,荣春兰,刘宁.ZrC含量对TiC基金属陶瓷组织和性能的影响[J].硬质合金,2007(02):65-69,128.
[4] Ettmayer P;Kolaska H;Lengauer W et al.Ti(C,N)Cermets-Metalhrgy and Properties[J].Int J Refra Met Hard Mater,1995,13:343-351.
[5] Xiong J;Cuo Z X;Shea B L et al.The effect of WC,Mo2C,TaC content on the microetntcmre and properties of ultra-fine TiC0.7C0.3 cermet[J].Materials & Design,2007,28:1689-1694.
[6] 刘宁,黄新民,周杰,田春艳,熊惟皓,张杰,崔昆.Ti(C,N)基金属陶瓷显微组织的研究[J].硅酸盐学报,1999(06):750-756.
[7] 章晓波,刘宁.Mo含量对Ti(C,N)基金属陶瓷组织和性能的影响[J].硬质合金,2006(03):160-163.
[8] 周玉.陶瓷材料学[M].北京:科学出版社,2004:210-216.
[9] 贾成厂.陶瓷基复合材料导论[M].北京:冶金工业出版社,2002:77-81.
[10] Park S;Kang S .Toughened ultra-fine (Ti,W)(C,N)-Ni cermets[J].Scripta Materialia,2005,52:129-133.
[11] Fu C T;Li A K;Wu J M .Effects of oxidation of Cr3C2 particulate-reinforced alumina composites on micrcetntcture and mechanical properties[J].Journal of Materials Science,1993,28:6285-6294.
[12] Reimaah I E .A review of issues in the hacture of haerfadal ceramice and ceramic comnicoompcsltes[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1997,237:159-167.
[13] 陈名海,刘宁,许育东.金属/陶瓷润湿性的研究现状[J].硬质合金,2002(04):199-205.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%