研究了稀土Y离子注入对FeCr,FeCrAl及NiCr合金高温抗氧化性能的影响.结果表明,对于主要形成Cr2O3膜的FeCr和NiCr合金,通过离子注入Y可以明显提高其高温抗氧化性能,但对形成Al2O3膜的FeCrAl合金,离子注入对合金抗氧化性能没有影响,添加稀土Y则使FeCrAl合金抗氧化性能大大提高.分析了氧化前、后氧化膜结构变化,认为早期形成的Y2O3膜对高温氧化时金属离子的扩散有不同的影响.
参考文献
| [1] | 李碚;颜玉新 .RE对Fe-Cr-Al合金α-Al2O3层晶粒生长的影响[J].金属学报,1984,20:B71. |
| [2] | 李碚;骆继群 .稀土对FeCrAl合金氧化皮形貌的影响[J].金属学报,1980,16:401. |
| [3] | Kung S C;Srinivasan V .The effect of yttrium on scale formation and breakdown of Fe-Cr-Al in mixed gas[J].Oxidation of Metals,1990,33:481. |
| [4] | Bennett M J;Houlton M R;Dearnaley G .The influence of the surface ion implantation of aluminium and yttrium upon the oxidation behaviour of a Fe-15%Cr-4%Al FECRALLOY stainless steel in air at 1100℃[J].Corrosion Science,1980,20:69. |
| [5] | Hampikian J M;Potter D I .The effects of yttrium ion implantation on the oxidation of nickel-chromium alloys I.the microstructure of yttrium implanted nickel-chromium alloys[J].Oxidation of Metals,1992,38:125. |
| [6] | Yang C H;Welsch G;Mitchell T E .Early stage of oxidation of yttrium-implanted Ni-20%Cr[J].Journal of Materials Science,1990,25:1724. |
| [7] | 李碚;颜玉新;高怀荪 .Ce对Fe-Cr合金高温氧化行为的影响[J].中国腐蚀与防护学报,1985,5(02):100. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%