采用国内(A，B)及国外(C)的孔密度为62cell/cm2堇青石蜂窝陶瓷载体作为研究对象，对三种载体的表面进行改性。在自制的铝胶中添加了适量的含La等混合稀土，测定其物理、化学性能的变化，结果证明：表面积和热稳定性随改性剂的配比不同而不同；载体C在晶相结构、孔壁厚度及TSP循环次数均优于A，B。用上述表面改性的载体制成的车用催化器，经测定，热劣化系数≤1.08，初活性CO、THC、NOx均大于90%。
The studies on the surface area of the three substrates were discussed.The adoptive substrates were porous cordierites produced in china (A,B) and from abroad(C) with cell density of 62cell/cm2. The samples of A,B and C were impregnated in the alumina solution kneading with the rare earth oxides,and their physical and chemical properties were tested.The results shows that the rare earth oxides were effective additives for improving the surface area and thermal stability,and the substrates C was much superior to A and B in the crystal structure,length on a side and TSP.The catalytic convector prepared in this method with active elements has the 90% conversion of CO,HC,NOx,the coeffcient of heated deterioration≤1.08.
参考文献
| [1] | John S Howitt.In Automotive Catalyst Supports,Catalysis and Automotive Pollution Control[M].Netherlands:Elsevier Science P,1978 |
| [2] | 潘履让.固体催化剂的设计与制备[M].天津:南开大学出版社,1996 |
| [3] | Miyoshi N;Matsumotos;Ozawa M et al.[J].SAE Technical Paper,1989,891970 |
| [4] | Ismagilov Z R;shkrabina R A;Koryabkina N A et al.[J].Catalysis Today,1995,24(03):269. |
| [5] | Ozawa M;Kimura M .[J].Journal of Materials Science Letters,1990,9(03):291. |
| [6] | 郑菁英;刘长林 .混合轻稀土燃烧催化剂的研究与应用[J].环境化学,1991,10(05):6. |
| [7] | 郑菁英;桑鸿勋.稀土添加物对催化燃烧作Pd/γ-Al2O3催化剂活性的影响[A].南京,1984 |
| [8] | 刘长林;李佩珩 .轻稀土氧化物-钯催化剂对一氧化碳的氧化作用[J].北京工业大学学报,1997,23(01):55. |
| [9] | Semmers J C;Williamson W B.Palladium-Only Catalysts for Closed-Zoop Control[A]. |
| [10] | 李春鸿.稀土在去除NO催化剂中的应用[J].有色金属与稀土应用,1994:1. |
| [11] | 李佩珩;刘长林.汽车催化转化器的研究与应用[J].世界汽车,1998(12):25-27. |
| [12] | 李佩珩,阎红,傅昕,曾潞,郑菁英.后处理工艺对Pd催化剂活性的影响[J].北京工业大学学报,2000(03):63-67. |
| [13] | 李佩珩;阎红;刘长林.关于中国汽车三元催化净化器产业化问题探讨[A].昆明,1990 |
| [14] | 薛群山;宵彦;谭克勤.氧化铈对三效催化剂性能的影响[A].,1990 |
| [15] | 汪文栋,林培琰,伏义路,俞寿明,孟明.含铈、镧低贵金属含量三效催化剂的结构与性能[J].催化学报,1999(05):525-529. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%