研究了渗稀土激光熔凝复合处理对纯铁表面耐磨性能及微观组织的影响。结果表明，经过复合处理，纯铁表面的耐磨性显著提高，磨损失重为未处理试样的5%，且纯铁表层微观组织改善，晶粒细化，组织均匀致密，渗入元素浓度梯度明显减小。
This paper studies the effects on pure Fe surface and the microstructure using the method of permeating RE combined with laser melting modification.The results show that after treated,the abrasion of treated sample has been improved significantly and the loss of weight has been reduced to 5%.The microstructure has improved been to be denser and more uniform than that of untreated,grain has been refined and the concentration gradient of the elements permeated has been decreased obviously.
参考文献
| [1] | 纪箴.钢中加入稀土对渗碳层的影响[J].稀土,1996(01):18. |
| [2] | 李全安.CeO2对M2+4B激光合金化层显微组织和耐磨性的影响[J].中国稀土学报,1995(03):280. |
| [3] | 沈以赴.稀土在激光熔覆涂层中的分布和行为[J].中国稀土学报,1997(04):344. |
| [4] | 王昆林;张庆波;朱允明 等.La2O3对镍基合金激光熔覆层耐蚀性的影响[J].中国腐蚀与防护学报,1998,18(03):237-240. |
| [5] | 陆建;倪晓武;贺安之 .高功率激光与材料相互作用机理研究进展[J].激光技术,1996,20(03):181-184. |
| [6] | Janez Grum;Roman Sturm .Laser surface melt-harding of gray and nodular irons[J].Applied Surface Science,1997,109/110:128-132. |
| [7] | 钟华仁.钢的稀土化学热处理[M].北京:国防工业出版社,1998:1-19. |
| [8] | 许越;韦永德;宋成璞 .稀土对20钢、45钢表面耐蚀性的影响[J].中国稀土学报,1993,1(01):52-55. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%