Gd5Si2Ge2合金的发现为常温范围磁制冷实用化发展提供了可能,然而其居里温度有待进一步提高.本文就添加钒进行合金化对它的改性作用开展了初步研究.结果表明:Gd5(Si2-xGe2-xV2x)合金(x≤0.03)能保持母相Gd5Si2Ge2的晶体结构,但显微组织却随钒的加入而发生显著改变;钒合金化使合金居里温度由～3℃提高到～18℃,同时磁化强度水平升高,居里点附近磁化强度变化陡度增大.
参考文献
| [1] | 徐光宪.稀土[M].北京:冶金工业出版社,1995:109. |
| [2] | Pecharsky VK;Gschneidner KA .Giant magnetocaloric effect in Gd-5(Si2Ge2)[J].Physical review letters,1997(23):4494-4497. |
| [3] | Pecharsky VK;Gschneidner KA .Tunable magnetic regenerator alloys with a giant magnetocaloric effect for magnetic refrigeration from similar to 20 to similar to 290 K[J].Applied physics letters,1997(24):3299-3301. |
| [4] | Pecharsky V K;Gschneidner K A .Effect of alloying on the giant magnetocaloric effect of Gd5(Si2Ge2)[J].Journal of Magnetism and Magnetic Materials,1997,167:1179. |
| [5] | Holtzberg F;Gambino R J;McGurie T R .New ferromagnetic compounds in the rare earth silicon and germanium systems[J].Journal of Physics and Chemistry of Solids,1967,28:2283. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%