研究了Pr含量对快淬Prx(FeCoZr)94-xB6(x=12.5,12,10.5,9.0)系列粘结磁体磁性能的影响.采用部分过快淬加晶化退火工艺,获得由非晶和微晶组成的条带,晶化处理后制备出最佳磁性能的磁体.随Pr含量的减少,磁体的内禀矫顽力Hci下降而剩磁Br增加,Pr含量低于10%,Br增加缓慢,Hci和(BH)m迅速下降.所以,10%是磁性能发生大的转变的临界Pr含量值,验证了作者提出的完全耦合软磁相体积分数模型.
参考文献
| [1] | Satoshi Hirosawa;Yutaka Matsuura;Hitoshi Yama-moto et al.Magnetization and magnetic anisotropy of R2Fe14B measured on single crystals[J].Journal of Applied Physics,1986,59(03):873-878. |
| [2] | Davies H A;Betancourt R J I;Harland C L .Nanophase (Nd/Pr)2Fe14B/α-Fe alloys:arttractive materials for isotropic magnets with enhanced properties[J].Scripta Materialia,2001,44:1337-1340. |
| [3] | Zhang Wengyong;Zhang shaoying;Yan A Yu et al.Effect of the substitution of Pr for Nd on microstructure and magnetic properties of nanocomposite Nd2Fe14B/α-Fe magnets[J].Journal of Magnetism and Magnetic Materials,2001,225:389-393. |
| [4] | Chen Zhongmin;Zhang Yong;Ding Yuquan et al.Studies on magnetic properties and microstructure of melt-spun nanocomposite R8(Fe,Co,Nb)86B6 magnets[J].Journal of Magnetism and Magnetic Materials,1999,195:420-427. |
| [5] | Kneller E.F.;Hawig R. .The exchange-spring magnet: a new material principle for permanent magnets[J].IEEE Transactions on Magnetics,1991(4):3588-3560. |
| [6] | Schrefl T;Fidler J;Kronmuller H .Remanence and coercivity in isotropic nanocrystalline permanent magnets[J].Physical Review B,1994,49:6100-6110. |
| [7] | Neu V;Hubert A;Schultz L .Modelling of enhanced remanence of nanocrystalline,exchange-coupled hard magnetic grains[J].Journal of Magnetism and Magnetic Materials,1998,189:391-396. |
| [8] | 刘颖,查五生,高升吉,连利仙,涂铭旌.稀土含量对快淬（Nd,Pr）x（FeCoZr）94-xB6粘结磁体磁性能的影响[J].中国稀土学报,2003(05):522-525. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%