采用快淬和晶化退火法制备了成分为Nd8.5Fe74.5Co5Cu1Nb1Zr3Cr0.5B6.5的纳米晶复合永磁合金.研究了制备过程中快淬速度和退火温度对合金磁性能和组织结构的影响.结果表明,快淬速度为16.7m/s,合金样品经690℃/4min的晶化处理后,制成的粘结磁体可得到较优异的综合磁性能:Br=0.65T,JHc=708.4kA/m,(BH)max=72.0kJ/m3.
参考文献
| [1] | Schreft T et al.Two-and three-dimensional calculation of remanence ehancement of rare earth based composite magnets(invite)[J].Journal of Applied Physics,1994,76(10):7053. |
| [2] | Zhongmin Chen et al.Effect of wheel speed and subsequent annealing on the microstructure and magnenetic properties of nanocomposite Pr2Fe14B/α-Fe[J].Journal of Magnetism and Magnetic Materials,1999,206:8-16. |
| [3] | Angela D. Barra-Barrera;Regina K. Murakami;Valquiria Villas-Boas .Optimization of the magnetic properties of nanocrystalline Pr_(5)Fe_(77-x)Cr_(x)B_(18) alloys[J].Journal of Magnetism and Magnetic Materials,2001(2):1428-1430. |
| [4] | Tiemin Zho et al.Quenchability and magnetic properties of Nd4Fe82B14[J].Journal of Materials Science and Technology,1998,14:235. |
| [5] | Akira Arai et al.High-energy isotropic resin bondedmagnets produced from (Nd,Dy)-(Fe,Co)-B nanocomposite alloys[J].IEEE Transactions on Magnetics,2001,37(04):220. |
| [6] | Choong Jin Yang;Eon Byung Park .Enhancement of magnetic properties of Fe/sub 3/B/Nd/sub 2/Fe/sub 14/B magnet by the addition of Co[J].IEEE Transactions on Magnetics,1999(5):3328-3330. |
| [7] | Hirosawa S.;Kanekiyo H.;Shigemoto Y.;Murakami K.;Miyoshi T.;Shioya Y. .Solidification and crystallization behaviors of Fe3B/Nd2Fe14B-based nanocomposite permanent-magnet alloys and influence of micro-alloyed Cu, Nb and Zr[J].Journal of Magnetism and Magnetic Materials,2002(1/3):424-429. |
| [8] | Hirosawa S;Kanekiyo H .Nanostructure and magnetic properties of chromium-doped Fe3B-Nd2Fe14B exchange-coupled permanent magnets[J].Materials Science and Engineering A,1996,217(367) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%