研究了利用速凝(SC)工艺以及速凝工艺结合氢破碎(HD)工艺制备NdFeB磁体的性能和微观结构.结果发现,单独引入SC工艺虽然保证了母合金α-Fe不析出,其成分不发生偏析,但是由于其特殊的微观组织结构,利用机械破碎的方法制粉容易使粉末多以多晶的状态出现,这不仅使磁体取向度降低,并使烧结磁体主相晶粒内分布有大量富钕相,这种现象必然影响到磁体的矫顽力.把SC工艺和HD工艺结合起来,可以有效地解决这个问题.
参考文献
| [1] | 李波,郭炳麟,王东玲,刘涛,林德,喻晓军.退火处理对速凝薄片显微组织的影响[J].稀有金属,2003(05):528-530. |
| [2] | Hirose Y;Hasegawa H;Sasaki S.Microstructure of strip cast alloys for high performance NdFeB magnets[A].,1998:77. |
| [3] | Sasaki S;Hasegawa H;Hirose Y .Method for producing casing alloy and magnet[P].US:5963774,1999-10-05. |
| [4] | Sagawa M;Hirose Y;Hasegawa H.Process for high energy NdFeB sintered magnets[A].Hanoi:IWOMS'99,1999:60-65. |
| [5] | Pollard R J;Oesterreicher H .Novel recording media Fe14Nd2B particles[J].IEEE Transactions on Magnetics,1986,22:735-737. |
| [6] | Pareti L;Moze O .Effects of hydrogen absorption on 3d and 4f anisotropies in RE2Fe14B(RE=Y,Nd,Ho,Tm)[J].Journal of the Less-Common Metals,1988,142:187-194. |
| [7] | 李波,郭炳麟,喻晓军,林德,王东玲,王新林.NdFeB永磁体取向度的测试方法[C].第十一届全国磁学和磁性材料会议论文集,2002:240-241. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%