采用甘氨酸-硝酸盐法合成La0.8Ca0.2CrO3复合氧化物粉料,对合成产物的晶体结构和显微形貌进行表征,研究烧成温度对La0.8Ca0.2CrO3相对密度和电导率的影响.实验结果表明,烧成温度为1400℃时样品即达较高的相对密度(92.6%),测试温度为800℃时样品的电导率为31.1 S·cm-1.与常规固相法相比,GNP法合成产物的纯度高、颗粒细(100nm～200nm),有良好的烧结活性,能够有效地降低材料的烧成温度和提高材料的电性能.
参考文献
| [1] | Faduska W;Isenberg A O .High temperature solid oxide fuel cell-technical status[J].Journal of Power Sources,1983,10(01):89-102. |
| [2] | Minh N Q .Ceramic fuel-cells[J].Journal of The American Chemical Society,1993,76(03):563-588. |
| [3] | Yokokawa H;Sakai N et al.Chemical thermodynamic considerations in sintering of LaCrO3-based perovskites[J].Journal of the Electrochemical Society,1991,138(04):1018-1027. |
| [4] | Yasuda I;Hikita T .Electrical concuctivity and defect structure of calcium-doped lanthanum chromites[J].Journal of the Electrochemical Society,1993,140(06):1699-1704. |
| [5] | Groupp L;Adersen H U .Densification of La1-xSrx CrO3[J].Journal of The American Chemical Society,1976,59(9-10):449-450. |
| [6] | Chick L A;Liu J et al.Phase transition and transient liquid-phase sintering in calcium-substituted lanthanum chromite[J].Journal of The American Chemical Society,1997,80(08):2109-2120. |
| [7] | Huang Duan-ping;Xu Qing;Jiang Jin-guo et al.Characterization of perovskite type composite oxides of La0.6Sr0.4Fe0.8Co0.2O3 Synthesized by the glycine-nitrate process[J].Journal of Chinese Ceramics Society,2002,30(zk):8-11. |
| [8] | Sakai N;Kawada T et al.Thermal expansion of some chromium deficient lanthanum chromites[J].Solid State Ionicis,1990,40-41:394-397. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%