以纳米镧镍氧化物前驱体和甲苯为反应物,氢化钙为还原剂,在不锈钢反应釜中于600℃溶剂热条件下成功地合成了棒状LaNiC2.运用XRD,TEM和SEM等对样品的结构和微观形貌进行了分析,并对样品进行了磁性测试.实验结果表明,此方法合成的LaNiC2材料呈棒状、具有铁磁性,同时该法具有简便易行、反应条件温和以及能耗低等优点.
参考文献
[1] | Iwamoto Y.;Ueda K.;Kohara T.;Iwasaki Y. .Microscopic measurements in La-139-NQR of the ternary carbide superconductor LaNiC2[J].Physics Letters, A,1998(4/6):439-442. |
[2] | Lee W H;Zeng H K;Yao Y D et al.Superconductivity in the Ni based ternary carbide LaNiC2[J].Physica C,1996,266:138-142. |
[3] | Koshikawa Y.;Kosaka M.;Yamauchi H.;Ohashi M.;Yamaguchi Y.;Onodera H. .CRYSTALLINE ELECTRIC FIELDS AND MAGNETIC PROPERTIES OF SINGLE-CRYSTALLINE RNIC2 COMPOUNDS (R=HO, ER AND TM)[J].Journal of Magnetism and Magnetic Materials,1997(1/2):72-82. |
[4] | Xie Y;Qian Y T et al.A benzene-thermal synthetic route to nanocrystalline GaN[J].Science,1996,272:1926-1927. |
[5] | Li Y D;Qian Y T;Liao H et al.A reduction-pyrolysis-catalysis synthesis of diamond[J].Science,1998,281:246-247. |
[6] | Wang W Z;Geng Y;Yan P et al.A novel mild route to nanocrystalline selenides at room temperature[J].Journal of the American Chemical Society,1999,121:4062-4063. |
[7] | Qian XF.;Wang C.;Xie Y.;Qian YT.;Zhang XM. .The preparation and phase transformation of nanocrystalline cobalt sulfides via a toluene thermal process[J].Inorganic Chemistry: A Research Journal that Includes Bioinorganic, Catalytic, Organometallic, Solid-State, and Synthetic Chemistry and Reaction Dynamics,1999(11):2621-2623. |
[8] | 米远祝,刘应亮,肖勇,袁定胜,张静娴.溶剂热制备条件对镍晶体结构的影响[J].无机化学学报,2005(04):603-606. |
[9] | 刘胜峰,吕俊芳,林建华,苏勉增.LaNi5类合金的软化学合成[J].化学通报,2000(10):34-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%