采用前驱体微波加热法、电阻加热法和传统的高温固相法等不同方法制备了Ca0.8Zn0.2TiO3:Pr3+荧光粉,以 TG-DSC、XRD、荧光光谱和粒度分析为表征手段,比较了不同方法制备Ca0.8Zn0.2TiO3:Pr3+的发光性质.XRD测定结果表明, 前驱体微波加热法和电阻加热法制备的样品可使反应温度低200℃,但材料的晶体化程度不高.TG-DSC的测定结果表明,前驱体在加热达到700℃以上才完全失重.荧光光谱和粒度分析的测定结果表明,与传统的高温固相法制备的荧光粉相比, 前驱体微波加热法和电阻加热法制备的荧光粉具有发光增强和颗粒细小均匀的特点,但微波加热法更为简单.
参考文献
[1] | Matsuzawa T.;Takeuchi N.;Murayama Y.;Aoki Y. .NEW LONG PHOSPHORESCENT PHOSPHOR WITH HIGH BRIGHTNESS, SRAL2O4-EU2+,DY3+[J].Journal of the Electrochemical Society,1996(8):2670-2673. |
[2] | Jia W;Yuan H et al.Crystal growth and characterization of SrAl2O4:Eu2+,Dy3+ and CaAl2O4:Eu2+,Nd3+ by the LHPG method[J].Journal of Crystal Growth,1999,200:179-184. |
[3] | Diallo PT.;Mahiou R.;Cousseins JC.;Boutinaud P. .RED LUMINESCENCE IN PR3+-DOPED CALCIUM TITANATES[J].Physica Status Solidi, A. Applied Research,1997(1):255-263. |
[4] | Royce M R;Matsuda S;Tamaki H .Red emitting long decay phosphors[P].US 5650094,1997-07-22. |
[5] | Diallo PT.;Boutinaud P.;Mahiou R.;Cousseins JC.;Jeanlouis K. .Improvement of the optical performances of Pr3+ in CaTiO3[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(0):218-222. |
[6] | Pan YX.;Su Q.;Xu HF.;Chen TH.;Ge WK.;Yang CL.;Wu MM. .Synthesis and red luminescence of Pr3+-doped CaTiO3 nanophosphor from polymer precursor[J].International Journal of Quantum Chemistry,2003(1):69-73. |
[7] | Cho S H;Yoo J S;Lee J D .Synthesis and low-voltage characteristics of CaTiO3:Pr luminescent powders[J].Journal of the Electrochemical Society,1996,143(10):231-234. |
[8] | Okamoto S;Kobayashi H;Yamamoto H .Enhancement of characteristic red emission from SrTiO3:Pr3+ by Al addition[J].Journal of Applied Physics,1999,86(10):5594-5597. |
[9] | Kim J Y;Jeon D Y;Kang S G et al.Morphology and cathodoluminescence of Li-doped SrTiO3:Pr,Ga a red phosphor operating at low voltage[J].Materials Research Society Symposium Proceedings,2001,667:G3.7.1-G3.7.5. |
[10] | Shinji Okamoto;Hajime Yamamoto .Emission from BaTiO_(3):Pr~(3+) controlled by ionic radius of added trivalent ion[J].Journal of Applied Physics,2002(8):5492-5494. |
[11] | 廉世勋,林建华,苏勉曾.Ca1-xZnxTiO3∶Pr3+, R+(R+=Li+, Na+, K+, Rb+, Cs+, Ag+)的合成和发光性质[J].中国稀土学报,2001(06):602-605. |
[12] | 李秀英,廉世勋,刘利民,朱爱玲,李承志,张华京,尹笃林.红色长余辉发光材料Ca2Zn4Ti15O36∶Pr3+的合成和发光性质[J].中国稀土学报,2005(01):16-20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%