采用溶胶-凝胶法制备了一系列钆、锆复合掺杂钛酸钡BaTi0.9Zr0.1O3·xGd2O3粉体及陶瓷,经SEM形貌观察,致密性较好.用XRD对粉体进行表征,所得晶相属四方相,随着钆和锆的掺入,粉体粒径变小.探讨了掺杂比例对其介电性能的影响,掺杂量x=0.004时εmax=8150.介温曲线的研究表明,居里峰前移,室温介电常数较大提高,介电温度稳定性好.
参考文献
| [1] | Michael Z C Hu;Kurian V;Andrew Payzant E et al.Wet chemical synthesis of monodispersed barium fitanate particles-hydrothermal conversion of TiO2 microspheres to nanocrystalline BaTiO3[J].Powder Technology,2000,110(1-2):2-14. |
| [2] | Buscaglia M T;Buscaglia V;Viviani M et al.Influence of foreign ions on the crystal structure of BaTiO3[J].Journal of the European Ceramic Society,2000,20(12):1997-2007. |
| [3] | Weat A R.固体化学及其应用[M].上海:复旦大学出版社,1989:392-413. |
| [4] | Fukai K;Hidaka K;Aoki M et al.Preparation and properties of uniform fine perovskite powders by hydrothermal synthesis[J].Ceramics International,1990,16(05):285-290. |
| [5] | 胡嗣强,黎少华.水热合成锆钛酸钡（BZT）固溶晶体的形成规律研究[J].化工冶金,1996(04):304-309. |
| [6] | 黄新友,高春华,陈祥冲,周浩伟,谭红根.二氧化铈掺杂锆钛酸钡陶瓷性能和结构的研究[J].电子元件与材料,2004(10):27-29. |
| [7] | 陈小兵;高维山;毛翔宇 .Y2O3掺杂BaTiO3陶瓷的介电特性[J].功能材料,1997,28(01):46-49. |
| [8] | Azizs Shaikh;Robert W Vest .Defect structure and dielectric properties of Nd2O3-modified BaTiO3[J].Journal of the American Ceramic Society,1986,69(09):689-694. |
| [9] | 齐建全,桂治轮,王永力,李琦,李龙土.Yb2O3的掺杂方式对Ba（Ti1--yZry）O3陶瓷介电性能的影响[J].无机材料学报,2001(05):989-992. |
| [10] | 郭炜,李玲霞,吴霞宛,王洪儒,张志萍.掺杂及工艺特性对高介BaTiO3系统性能的影响[J].压电与声光,2002(06):482-484. |
| [11] | 江涛,陈绍茂,郭育源.中温烧结BaTiO3基多相铁电瓷料X7R特性[J].华南理工大学学报（自然科学版）,1996(03):124. |
| [12] | 徐政;倪宏伟.现代功能陶瓷[M].北京:国防工业出版社,1998 |
| [13] | 王辉,崔斌,畅柱国,王小芳.软化学法制备钛酸钡粉体的研究进展[J].材料科学与工程学报,2003(05):773-776. |
| [14] | 杨飞宇,燕青芝,赵浩峰,葛昌纯.钛酸钡粉体制备方法研究进展[J].粉末冶金工业,2003(06):27-31. |
| [15] | 郭卫红;汪济奎.现代功能材料及其应用[M].北京:化学工业出版社,2002 |
| [16] | 郭炜,李玲霞,吴霞宛,王洪儒,张志萍.掺杂稀土元素对细晶BaTiO3系统耐压及介电性能的影响[J].中国稀土学报,2003(02):209-213. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%