以Ce(NO3)3·6H2O和NH4HCO3为原料,采用化学沉淀法制得了平均长度84nm,直径15nm的CeO2棒状晶.利用XRD、TEM对CeO2粉体及其前驱体进行分析表征,发现CeO2晶粒继承了前驱体的棒状形貌.借助FTIR确定了前驱体的化学组成为Ce2O(CO3)2·H2O,从化学反应过程出发研究了CeO2棒状晶的具体形成过程.
参考文献
| [1] | 王艳荣 .沉淀法制备纳米二氧化铈[D].成都理工大学,2004. |
| [2] | 梅燕,韩业斌,聂祚仁.溶液的pH值对纳米CeO2晶粒形貌及形成机制的影响[J].中国稀土学报,2006(01):43-47. |
| [3] | Z.H. Han;N. Guo;K.B. Tang .Hydrothermal crystal gowth and characterization of cerium hdroxycarbonates[J].Journal of Crystal Growth,2000(3):315-318. |
| [4] | Oikawa M;Fujihara S .Crystal growth of Ce2O(CO3)(2) center dot H2O in aqueous solutions: Film formation and samarium doping[J].International Journal of Quantum Chemistry,2005(6):2036-2041. |
| [5] | Hsien-Cheng Wang;Chung-Hsin Lu .Synthesis of cerium hydroxycarbonate powders via a hydrothermal technique[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2002(4):783-792. |
| [6] | Jianqing CHEN,Zhigang Chen,Jinchun LI.Morphology Controlling of the Ultrafine Cerium Dioxide (CeO2) Precursor[J].材料科学技术学报(英文版),2004(04):438-440. |
| [7] | 梅燕,韩业斌,聂祚仁.表面活性剂对均相沉淀法制备单晶Ce2O（CO3）2·H2O微粉形貌及形成机理的影响[J].化学物理学报,2006(03):269-272. |
| [8] | Zhu Zhaowu;Long Zhiqi;Zhang Shunli .Preparation of Fine Spherical Particle Sized Ceria by Precipitation Method with Ammonium Bicarbonate[J].Journal of Rare Earths,2005(1):81-84. |
| [9] | 陈志刚,陈建清,陈杨,李锦春.二氧化铈前驱体煅烧过程中的遗传性研究[J].江苏大学学报（自然科学版）,2004(06):536-540. |
| [10] | 李梅,柳召刚,刘铃声,胡艳宏,武国琴,熊晓柏.氧化铈超细粉体的制备研究[J].中国稀土学报,2003(04):465-467. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%