采用化学共沉淀法制备了Ba0.5Sr0.5Co0.8Fe0.2-xCexO3(x=0,0.01,0.025,0.05)复合氧化物,用.XRD分析了材料的相结构,并用AV3618型微波矢量网络分析仪测试了样品在8.2GHz～12.5GHz范围内的微波吸收特性,结果表明,在1100℃煅烧后样品呈现出单一的钙钛矿型结构,铈的含量影响材料的吸波性能,当x=0.025时,Ba0.5Sr0.5Co0.8Fe0.2-xCexO3的吸波性能最佳,材料涂层厚度为1mm时,在测试频段内有三个吸收峰,最高的吸收峰位于9.06GHz处,吸收峰值达36.83dB,18dB以上频带宽度达2.2GHz,适量掺杂铈是提高该复合氧化物吸波性能的一种有效途径.
参考文献
| [1] | 邢丽英.隐身材料[M].北京:化学工业出版社,2004:172-176. |
| [2] | Olmedo L;Chateau G;Deleuze C et al.Microwave characterization and metallization of magnetic granular materials[J].Applied Physics,1993,73(10):6992-6994. |
| [3] | Cho SB.;Oh JH.;Kang DH. .RELATIONSHIP BETWEEN MAGNETIC PROPERTIES AND MICROWAVE-ABSORBING CHARACTERISTICS OF NIZNCO FERRITE COMPOSITES[J].Journal of Materials Science,1996(17):4719-4722. |
| [4] | Wang Xiao hua;Xiong Gang;Wang Xin et al.Preparation and magnetic properties of BaZn2-xCoxFe16O27 nanocrystalline powders by the stearic acid gel method[J].Journal of Magnetism and Magnetic Materials,1998,189:9698. |
| [5] | 何玉平,胡国光,姚学标,尹萍.BaMnZnCoTi-W型铁氧体微波吸收剂的制备和特性研究[J].功能材料,2002(01):36-38. |
| [6] | 徐坚,熊惟皓,曾爱香,王采芳.稀土元素在磁性吸波材料中的应用研究进展[J].稀土,2004(06):68-73. |
| [7] | 苏海林.（Ni,Zn,Co）2-W型复合钡铁氧体的制备及其微波吸收特性[J].材料科学与工程,2002(04):568-571. |
| [8] | 刘方舒,赵敏光,陈凯锋,徐明.W型钡铁氧体的溶胶-凝胶法制备及吸波性能研究[J].材料导报,2006(z1):52-53. |
| [9] | 胡国光,尹萍,吕庆荣.LaxSr1-xMnO3氧化物的导电和吸收特性[J].中国稀土学报,2002(02):179-181. |
| [10] | 周克省,王达,尹荔松,孔德明,黄可龙.La0.8Sr0.2 Mn1-yFeyO3微波电磁特性与损耗机制[J].中国有色金属学报,2006(05):753-757. |
| [11] | 李嵩,季世军,孙俊才.共沉淀法合成新型阴极材料Ba0.5Sr0.5Co0.8Fe0.2O3-σ[J].稀有金属材料与工程,2006(03):492-495. |
| [12] | 黄永杰.磁性材料[M].北京:电子工业出版社,1994:200-203. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%