采用甩带法制备了具有<112>织构的稀土磁致伸缩速凝片,以速凝片为基础,从粘结剂的种类和用量、样品的固化工艺等方面系统地研究了粘结稀土磁致伸缩材料的制备工艺,确定了较适宜的粘结剂用量为重量百分比4%,较好的固化工艺为150℃×2h.
The rare earth magnetostrictive flakes with <112>fabric have been prepared by strip-casting method. Using strip-casting flakes,preparing technique of bonding rare earth magnetostictive materials has been studied systemically on the type and amount of bonder and curing processes of the samples. It is verified that the suitable proportion of bonder in the sample is about 4 percentage in weight,the optimal curing process is 150℃×2h.
参考文献
| [1] | Y. P. Wan;Z. Zhong;D. N. Fang .Permeability dependence of the effective magnetostriction of magnetostrictive composites[J].Journal of Applied Physics,2004(6):3099-3110. |
| [2] | 鲍芳,李继容,王春茹.磁致伸缩器件及其应用研究[J].传感器技术,2001(08):1-3. |
| [3] | 王博文;葛景岩 .巨磁致伸缩材料及其应用[J].沈阳工业大学学报,1998,20(03):64-67. |
| [4] | Oh Yeoul Kwon;Hee Yeoun Kim;Seung II Cha;Soon Hyung Hong .Magnetostriction and magnetomechanical coupling of grain-aligned Tb_(0.33)Dy_(0.67)Fe_y/epoxy-filled composites[J].Journal of Applied Physics,2005(11):113905.1-113905.4. |
| [5] | 温永春,赵增祺,江丽萍,吴双霞,郝宏波.粘结Terfenol-D磁致伸缩材料制备工艺研究[J].稀土,2006(03):44-47. |
| [6] | 江丽萍,赵增祺,吴双霞,黄继民,温永春,左良.粘结稀土磁致伸缩材料制备工艺研究[J].稀土,2005(04):30-32. |
| [7] | 周寿增;蒋成保;李春和 等.稀土超磁致伸缩合金结晶形貌研究[J].金属热处理学报,1997,18(03):73-78. |
| [8] | 蒋成保;周寿增;张茂才 等.定向凝固TbDyFe合金的取向、组织和磁致伸缩性能[J].金属学报,1998,34(02):164-170. |
| [9] | 王德中.环氧树脂生产与应用[M].北京:化学工业出版社,2001 |
| [10] | 张开.高分子界面化学[M].北京:中国石化出版社,1996 |
| [11] | Y. Chen;J. E. Snyder;C. R. Schwichtenberg;K. W. Dennis;D. K. Falzgraf;R. W. McCallum;D. C. Jiles .Effect of the elastic modulus of the matrix on magnetostrictive strain in composites[J].Applied physics letters,1999(8):1159-1161. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%