研究了碳酸盐沉淀法制备超细氧化铈粉体的工艺.结果表明,采用碳酸盐正向沉淀法可以得到超细氧化铈粉体,其体积中心粒径D50为0.08μm、比表面积为59.489 m2·g-1,晶体结构为立方晶系,萤石型结构,形状为棒状,分散性较好.
参考文献
| [1] | Matijevic E;Has W P .Preparation of monodispersed colloidal particles of lanthanide compounds:Ⅰ.gadohnium,europium,terbium,samarium,and cerium(Ⅲ)[J].Journal of Colloid and Interface Science,1987,118:506-511. |
| [2] | Hirano M;Kato E .Hydrothermal synthesis of nanocrystalline cerium(Ⅳ)oxide powers[J].J Am Cweam Soc,1999,82(03):786-790. |
| [3] | T. Masui;H. Hirai;N. Imanaka;G. Adachi;T. Sakata;H. Mori .Synthesis of cerium oxide nanoparticles by hydrothermal crystallization with citric acid[J].Journal of Materials Science Letters,2002(6):489-491. |
| [4] | Kuribayashi K;Uchikawa R;Akahashi K .Preparation of cerium dioxide thin films via sol-gel process and their characteristics electriealbuffer layers[J].Journal Ceramic Society,1999,107(03):275-277. |
| [5] | 石硕,鲁润华,汪汉卿.W/O微乳液中CeO2超细粒子的制备[J].化学通报,1998(12):51-53. |
| [6] | 潘湛昌,杨文霞,张环华,肖楚民.纳米二氧化铈的电化学制备与表征[J].化工新型材料,2004(10):31-33,50. |
| [7] | 董相廷,刘桂霞,孙晶,闫景辉,洪广言.透明纳米CeO2的合成与表征[J].中国稀土学报,2002(02):123-125. |
| [8] | 徐华蕊.用喷雾反应法制备实心球形氧化铈超细粉末[J].稀土,1999(06):29. |
| [9] | 焦小燕,罗贤满,杨宇俊,辜子英,李永绣.碳酸氢钠沉淀镧及碳酸镧的结晶过程研究[C].中国稀土科技进展（中国稀土学会第四届学术年会：论文专辑）,2000:149～154. |
| [10] | 何小彬,李永绣.碳酸镨的结晶活性、外观形貌及结晶生长机制[J].中国稀土学报,2002(z3):95-98. |
| [11] | 黄婷 .碳酸钇、碳酸钕的结晶及相关技术研究[D].南昌大学,2005. |
| [12] | 李永绣,胡平贵,何小彬,辜子英,黎敏.碳酸钇铵复盐结晶的形成及影响因素[J].中国稀土学报,2000(01):79-81. |
| [13] | 于德才;洪广言;董相廷 等.碳酸盐沉淀法制备稀土氧化物超微粉末[P].中国专利:CN102805C,1996. |
| [14] | 李梅,柳召刚,刘铃声,胡艳宏,武国琴,熊晓柏.氧化铈超细粉体的制备研究[J].中国稀土学报,2003(04):465-467. |
| [15] | 张顺利,黄小卫,崔大立,罗永.碳酸氢铵沉淀法制备氧化钇粉体时反应条件对产物粒度的影响[J].中国稀土学报,2003(06):643-646. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%