采用氨水一草酸协同沉淀法制备了CeO2超细粉体材料.用正交试验研究了制备条件对粉体性能的影响,得到最佳的制备条件.并用XRD、SEM、粒度测试等对其进行了表征.结果表明,所制备的超细CeO2粉末颗粒细小均匀,形状完整,具有完整的晶格.体积中心径D50为0.139μm,最大粒径约为1.5μm,基本上呈正态分布.
参考文献
| [1] | 李永绣,周新木,辜子英,彭德院,胡平贵,周雪珍,焦晓燕,何小彬,魏坤,刘桂华.稀土抛光材料的生产、应用及其新进展[J].稀土,2002(05):71-74. |
| [2] | Powell B R;Bloink R L;Eickel C C .Preparation of cerium dioxide for catalyst support[J].Journal of the American Ceramic Society,1988,71(02):C104-C106. |
| [3] | 钟莹;王成云 .稀土纳米材料研究进展[J].深圳大学学报(理工版),2000,17(04):68-73. |
| [4] | Herle J V;Horita T;Kawada T et al.Fabrication and sintering of fine yttria doped ceria powdcr[J].Journal of the American Ceramic Society,1997,80(04):933-940. |
| [5] | 景晓燕;洪广言 .醇盐法制备稀土化合物超微粉末[J].应用化学,1990,7(02):92-94. |
| [6] | 李梅,柳召刚,胡艳宏,刘铃声,熊晓柏,邱巨峰.Preparation and Characterization of CeO2 Superfine Powder[J].稀土学报(英文版),2003(06):654-656. |
| [7] | Chen JM.;Lin JY.;Hong IP.;Chang CF.;Yang HD.;Nachimuthu P. .Origin of size effect on superconductivity in (R-0.8 Pr-0.2)Ba2Cu3O7 studied by soft X-ray absorption spectroscopy[J].Chemical Physics Letters,2001(1/3):85-91. |
| [8] | 项可风;吴启光.试验设计与数据分析[M].北京:科学出版社,1989 |
| [9] | Paul C Hiemenz.胶体与表面化学原理[M].北京:北京大学出版社,1986 |
| [10] | 刘吉平;郝向阳.纳米科学与技术[M].北京:科学出版社,2003 |
| [11] | 董相廷,李铭,张伟,刘桂霞,洪广言.沉淀法制备CeO2纳米晶与表征[J].中国稀土学报,2001(01):24-26. |
| [12] | Baeetal D S .[J].Materials Letters,2002,56:610-613. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%