采用共沉淀法制备了不同铈锆比的粉末铈锆固溶体,考察了铈锆比和铈锆固溶体负载量对浸渍法制备的颗粒状和整体样贵金属催化剂上C3H6(丙烯)氧化反应催化性能的影响,并运用XRD和TPD表征技术对催化剂的物化性能进行研究.结果表明,所制备的催化剂中均形成了铈锆固溶体,并且铈锆含量的增加能够提高催化剂对C3H6的吸附能力.当铈锆固溶体的负载量相同时,在氧化气氛和较低贵金属含量条件下、Ceo.6Zro.4O2的加入使催化剂在低温时具有最好的催化效果.但与Pt/A12O3相比,采用浸渍法添加铈锆固溶体降低了贵金属整体样催化剂的活性,且活性随着负载量的增加显著降低.
参考文献
| [1] | 王建昕;傅立新;黎维彬.汽车排气污染治理及催化转化器[M].北京:化学工业出版社,2000 |
| [2] | Christine Bozo;Nolven Guihaume;Jean-Marie Herrmann .Role of the Ceria-Zirconia Support in the Reactivity of Platinum and Palladium Catalysts for Methane Total Oxidation under Lean Conditions[J].Journal of Catalysis,2001(2):393-406. |
| [3] | 李淑莲,李时瑶,吴春田,孙来生.汽车尾气净化用Pt/ZrO2-CeO2催化剂的表征与性能[J].催化学报,1999(01):67-69. |
| [4] | Juan R. Gonzalez-Velasco;Miguel A. Gutierrez-Ortiz;Jean-Louis Marc;Juan A. Botas;M. Pilar Gonzalez-Marcos;Gilbert Blanchard .Contribution of cerium/zirconium mixed oxides to the activity of anew generation of TWC[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,1999(3):167-178. |
| [5] | 张怀红,龚茂初,赵彬,郭家秀,陈耀强.铈锆比对贵金属催化剂Pt/CeO2-ZrO2性能的影响[J].贵金属,2004(04):17-21. |
| [6] | Sitthiphong Pengpanich;Vissanu Meeyoo;Thirasak Rirksomboon;Kunchana Bunyakiat .Catalytic oxidation of methane over CeO_2-ZrO_2 mixed oxide solid solution catalysts prepared via urea hydrolysis[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2002(1/2):221-233. |
| [7] | Trovarelli A.;Rocchini E.;de Leitenburg C.;Dolcetti G.;Boaro M. .Some recent developments in the characterization of ceria-based catalysts[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(0):584-591. |
| [8] | Du Y;Yashima M;Koura T et al.Thermodynamic evaluation of the ZrO2-CeO2 system[J].Scripta Metallurgica et Materialia,1994,31:327-332. |
| [9] | 肖莉,林培琰,杨志柏,汪文栋.Ce-Zr固溶体的纯度及其在三效催化剂中的作用[J].分子催化,2000(02):81-86. |
| [10] | 范恩荣 .催化燃烧方法概况[J].煤气与热力,1997,17(04):32-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%