通过调节镀液中不同的Ni/W比例、温度和沉积电流密度,研究在焦磷酸盐体系中镍钨合金电沉积的电流效率、沉积层组成和显微硬度.实验结果表明:合金共沉积的电流效率不高.为了尽量提高合金的沉积电流效率,主要途径宜增大镀液中硫酸镍和钨酸钠的浓度;提高合金沉积电流密度,降低镀液中[Ni]/[W]比例,则镀层中的钨含量增大;合金沉积层的显微硬度随镀层中的W含量提高而增大.
参考文献
| [1] | Lindsay J .Advanced Techniques for Replacing Chromium;3rd Information Exchange[J].Plating and Surface Finishing,1997,84(02):24-25. |
| [2] | M.El-Sharif .Replacing hexavalent chromium in electroplating[J].Transactions of the Institute of Metal Finishing,1997(6):B143-B147. |
| [3] | Croopnick G A;Scruggs D M .A Low Environmental-Risk Replacement for Chromium and Electroless Nickel[J].Metal Finishing,1994,92(04):13-16. |
| [4] | Osteryoung .Electrodeposition of Ni-W-B amorphous alloys[J].Journal of Applied Electrochemistry,1995,25(12):1091-1097. |
| [5] | 蔡积庆 .Ni-W系合金电镀[J].电镀与环保,1998,18(03):14-16. |
| [6] | 杨文,王晓东.非晶态Ni-W合金镀层电沉积影响因素和特性的研究[J].腐蚀科学与防护技术,1998(03):159. |
| [7] | 吴海玲 .镍钨合金电镀工艺[J].电镀与涂饰,1998,17(03):22-25. |
| [8] | M. Bratoeva;N. Atanassov .Nickel-tungsten alloy electrodeposition from a sulfamate electrolyte[J].Metal finishing,1998(6):92-99. |
| [9] | 杨防祖,曹刚敏,解建云,郑雪清,许书楷,周绍民.电流密度影响下镍钨合金电沉积层的组成、结构和形貌[J].厦门大学学报（自然科学版）,1999(01):56-60. |
| [10] | 陈国珍;黄贤智;刘文远.紫外可见分光光度法[M].北京:原子能出版社,1987:277. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%